Transparent PETG Plastics Sheets For High-end Credit Card Passport Cardbody Prodution
1. Introduction of Transparent PETG Plastics Sheets For High-end Credit Card Passport Cardbody Prodution
Transparent PETG Plastics Sheets For High-end Credit Card Passport
Cardbody Prodution is widely used in card base production. It has such features as
impact resistance, high temperature resistance, anti-static,
abrasion, folding and high strength. It is widely used for the
production of high-end credit cards, ID cards and passport, etc.
PETG is a kind of transparent amorphous copolyester.
| Item | PETG Core Sheet |
| Color | White |
| Thickness Range(mm) | 0.1-0.76 |
| Vicat point ℃ | 78-80 ± 2 |
| Tensile strength | ≥50 Mpa |
| Surface | Both sides matt |
| Density | 1.3 ± 0.05 |
| Transparency | ≤5 |
| Heat shrink | ≥-8.0 % (longitudinal) &≥-4.0 %(transverse) |
Features:
1).Excellent strength and wear-resisting
2).High temperature and low temperate resistance;
3).Perfect application for laser Engraving
4).Environment-friendly material
5).Longer service life
2.Specification of Transparent PETG Plastics Sheets For High-end Credit Card Passport Cardbody Prodution
The performance of PETG is quite different from PET and PC. PETG plate has outstanding toughness and high impact strength, its impact strength is 3-10 times more than ordinary plastic plate, and it has a wide processing range, high mechanical strength and excellent flexibility. Compared with PVC, it has high transparency, good luster and easy to print. At the same time, PETG has environmental protection advaes, and it can be recycled without polluting the environment. PETG sheet has low flammability, good fire resistance, no combustion support, low smoke emission, no harmful substances after combustion.
Technical Parameters:
| Item | Parameters |
| Vicat softening point (B50) | 78±2 |
| Vicat softening point (A120) | 80±2 |
| Heating Shrinkage ratio 105 ℃/10min | ≥-8.0 % (longitudinal) &≥-4.0 %(transverse) |
| Surface Dyne (dynes/cm) | ≥38 |
| Normal thickness in mm | 0.10-0.76 |
| Density (g/cm3) | 1.30 ±0.05 |
| Peel Strength (90°, 300mm/min) | ≥6.0 N/cm |
| Aging time (65℃ temp./95% humidity ) | ＞200 hours |
| Suitable ink | offset and silk screen printing UV ink, Pigment and dye ink for inkjet printing as well as digital printing ink |
3. Application of Transparent PETG Plastics Sheets For
High-end Credit Card Passport Cardbody Prodution
Used for the protecting layer of various kinds of PETG material cards.
Card-making method:
1). Print the patterns directly to the material
2). Laminate with overlay
3). Punching
4). Other art-work
| Item | Unit | Value | |
| Density | g/cm3 | 1.30 ±0.05 | |
| Tensile Strength | Horizontal | MPa | ≥50 |
| Vertical | ≥50 | ||
| Vicat | ℃ | 78-80 | |
| Surface Dyne | dynes/cm | ≥38 | |
| Thickness range | mm | 0.1-0.76mm | |
4. Packing of Transparent PETG Plastics Sheets For High-end Credit Card Passport Cardbody Prodution
Characteristic:
1.Good lamination properties
2.Good impact resistance
3.Good chemical resistance
4.Excellent printability with either offset or screen printing
5.Laminating Temp 120 degrees Celcius-130 degrees Celcius (lab conditions)