The 2-Flute Straight end mill have a mirror polish and large chip space which produces smooth cutting and fast chip-removal.
Up to 2.5X longer life compared to uncoated and has better temperature resistance and hardness
Carbide for maximum durability in abrasive material.
Up-cut spiral for optimum chip flow and improved finish on bottom of board.
Suitable for MDF,PVC,Acrylic, wood, solid wood, chipboard, plywood, organic board, core board, etc.
Widely used for cutting/engraving / carving/grooving/slotting/drilling /hollowing/positioning/roughing/milling.
Product Parameters
| HRC | HRC45/55/60/65 |
| Coating Type | ALTIN /TIALN /TISIN /NACO /DLC /Diamond |
| OEM | √ |
| Suitable For | All Kinds Matel Plastic Wood Acrylic and so on |
Super Raw Material
| Item | HRC50 | HRC55 | HRC60 | HRC65 |
| Grade | YG10X | YL10.2 & WF25 | Germany K44 &K40 | H10F |
| Details | Grain size 0.7um, Co10%, Flexural strength 3320N/mm2 | Grain size 0.6um, Co10%, Flexural strength 4000N/mm2 | Grain size 0.5um, Co12%, Flexural strength 4300N/mm2 | Grain size 0.5um, Co10%, Flexural strength 4300N/mm2 |
Super Coating
| Coating Classifying and Advantage | |||||
| Item | Coating Type | AlTin | TiAlN | TiSiN | Naco |
| Characteristic | Hardness(HV) | 3300 | 2800 | 4300 | 42(GPA) |
| Thickness(UM) | 2.5-3 | 2.5-3 | 3 | 3 | |
| Oxidation Temp.(°C) | 900 | 800 | 1000 | 1200 | |
| Friction Coefficient | 0.35 | 0.3 | 0.25 | 0.4 | |
| Color | Black | Dark Purple | Copper | Blue | |
| Advantages | High heat stability | Normally cutting | Suitable for heavy cutting, and high hardness cutting | For high precision Cutting | |
Suitable for high speed, dry cutting | Suitable for cutting mould steel, stainless steel | Suitable for high hardness cutting, mould steel processing | |||
Most suitable for carbide cutting tools, turning insert | |||||