The raw materials for C95400 Bronze Gleitlager Bearing Nuts typically consist of a high-quality alloy known as C95400 bronze. This alloy is composed of copper, tin, and other elements that provide excellent mechanical properties and wear resistance.
C95400 bronze is a lead-free tin-based bronze alloy that offers good machinability, high strength, and corrosion resistance. It is often chosen for applications that require bearing nuts to withstand heavy loads, high speeds, and variable operating conditions.
The raw materials for these bearing nuts are carefully selected and processed to ensure consistent quality and performance. They undergo various manufacturing processes such as casting, forging, or machining to form the desired shape and size of the bearing nut.
By using C95400 bronze as the raw material, the bearing nuts can be designed to meet specific requirements for load-bearing capacity, wear resistance, and durability. This makes them suitable for a wide range of industrial applications where reliable and long-lasting bearing nuts are essential.
| |||||||||
Cu | Sn | Al | Fe | Mn | Ni | Pb | Si | P | Zn |
Min83.0 | - | 10.5-11.5 | 3.0-5.0 | 0.5 | 1.5 | - | - | - | - |
Mechanical properties of | |||
|---|---|---|---|
Tensile strength(Mpa) | yield strength (Mpa) | elongation% | hardness(HB) |
248 | 131 | 15 |
60 |
| US Customary | Metric |
|---|---|---|
Melting Point - Liquidus | 1693 °F | 923 °C |
Melting Point - Solidus | 1625 °F | 885 °C |
Density | 0.283 lb/in3 at 68 °F | 7.83 gm/cm3 at 20 °C |
Specific Gravity | 7.83 | 7.83 |
Electrical Conductivity | 8% IACS at 68 °F | 0.046 MegaSiemens/cm at 20 °C |
Thermal Conductivity | 20.5 Btu/sq ft/ft hr/°F at 68 °F | 35.5 W/m at 20 °C |
Coefficient of Thermal Expansion 68-572 | 12 · 10-6 per °F (68-572 °F) | 20.7 · 10-6 per °C (20-300 °C) |
Specific Heat Capacity | 0.09 Btu/lb/°F at 68 °F | 377.1 J/kg at 20 ° |
Modulus of Elasticity in Tension | 14200 ksi | 97900 MPa |
Magnetic Permeability* | 1.09 | 1.09 |
Used in the manufacture of hydraulic valves, stem, gear pumps, vane pumps, piston pumps, oil cylinders and so on
Automobile: Turbocharger, engine, automobile air conditioning compressor, vehicle bridge
Basic industry: bearing retainer, bearing bush, bolt, nut, washer, worm wheel
Ship: propeller, propeller cap, worm wheel, Marine copper flange, copper shaft rod, copper sleeve
Construction machinery: rock drilling nuts, copper sleeve drill shank, wear-resistant sleeve moving parts
Railway: conductor bar, line guide, brake valve