The C95400 aluminum bronze bushing, available in both shoulder and straight designs, offers exceptional performance and durability for a wide range of industrial applications. Aluminum bronze, a unique alloy combining the properties of aluminum and bronze, exhibits high strength, corrosion resistance, and wear durability.
The shoulder design bushing features a raised or stepped portion that provides additional support and stability. This design is often used in applications where higher loads or additional alignment are required. The straight design, on the other hand, offers a more streamlined profile suitable for tight spaces or where a lower-profile bushing is preferred.
Both designs of the C95400 aluminum bronze bushing are precision-engineered to meet strict quality standards. They are manufactured using high-grade materials and advanced manufacturing techniques to ensure superior performance and long-lasting durability.
The bushings' aluminum bronze composition makes them ideal for use in environments that expose them to corrosive chemicals or high-temperature conditions. Their resistance to wear and abrasion also makes them suitable for high-speed or high-load applications.
Whether you need a shoulder or straight design, the C95400 aluminum bronze bushing is a reliable and cost-effective solution for improving the performance and durability of your mechanical systems. Its unique combination of properties and versatility makes it a popular choice for various industrial applications.
Graphite Impregnated Brass
C95400* Aluminum Bronze: C954 Aluminum Bronze Bear...
Copper Alloy Straight Thin Wall
| Part Number | L | MPBZ | MPBZU | |||||||||||||||||||||
| Type | dF7 | Dm6 (*1) | Thickness (N) | *Rotation Stopper Screw (Reference) | Dm6 (*1) | Thickness (N) | ||||||||||||||||||
| MPBZ MPBZU *L dimensions in ( ) are available only for MPBZ. | 5 | +0.022 +0.010 | 8 | (9) | 10 | 12 | (15) | 9 | 2 | M4x8 | 7 | 1 | ||||||||||||
| 6 | 8 | (9) | 10 | 12 | 15 | 16 | (19) | (20) | 10 | 8 | ||||||||||||||
| 8 | +0.028 +0.013 | 8 | (9) | 10 | 12 | 15 | 16 | (19) | 20 | (25) | 12 | 10 | ||||||||||||
| 10 | 8 | (9) | 10 | 12 | 15 | 16 | (19) | 20 | 25 | (30) | 14 | 12 | ||||||||||||
| 12 | +0.034 +0.016 | (8) | (9) | 10 | 12 | 15 | 16 | (19) | 20 | 25 | (30) | (35) | 18 | 3 | 15 | 1.5 | ||||||||
| 13 | (9) | 10 | 12 | 15 | 16 | (19) | 20 | 25 | (30) | (35) | 19 | 16 | ||||||||||||
| 15 | (9) | 10 | 12 | 15 | 16 | (19) | 20 | 25 | 30 | (35) | (40) | 21 | 18 | |||||||||||
| 16 | (9) | 10 | 12 | 15 | 16 | (19) | 20 | 25 | 30 | (35) | (40) | 22 | 20 | 2 | ||||||||||
| 18 | (9) | (10) | 12 | 15 | 16 | (19) | 20 | 25 | 30 | (35) | (40) | 24 | M5x8 | 22 | ||||||||||
| 20 | +0.041 +0.020 | (9) | (10) | (12) | 15 | 16 | (19) | 20 | 25 | 30 | (35) | 40 | (50) | (60) | 28 | 4 | 24 | |||||||
| 20A | (9) | (10) | (12) | (15) | (16) | (19) | (20) | (25) | (30) | (35) | (40) | (50) | 30 | 5 | - | |||||||||
| 25 | (12) | 15 | 16 | (19) | 20 | 25 | 30 | (35) | 40 | (50) | (60) | 33 | 4 | 29 | ||||||||||
| 25A | (12) | (15) | (16) | (19) | (20) | (25) | (30) | (35) | (40) | (50) | (60) | 35 | 5 | - | ||||||||||
| 30 | (12) | 15 | 16 | (19) | 20 | 25 | 30 | (35) | 40 | (50) | (60) | (70) | 38 | 4 | M6x16 | 34 | ||||||||
| 35 | +0.050 +0.025 | 20 | 25 | 30 | (35) | 40 | (50) | (60) | (70) | 44 | 4.5 | 40 | 2.5 | |||||||||||
| 40 | 20 | 25 | 30 | (35) | 40 | 50 | (60) | (70) | (80) | 50 | 5 | 45 | ||||||||||||
| 50 | 30 | (35) | 40 | 50 | (60) | (70) | (80) | 62 | 6 | M8x16 | 55 | |||||||||||||
| 60 | +0.060 +0.030 | (50) | (60) | (70) | (80) | 75 | 7.5 | - | - | |||||||||||||||
| 80 | (60) | (70) | (80) | 96 | 8 | - | - | |||||||||||||||||
| 100 | +0.071 +0.036 | (80) | (100) | 120 | 10 | - | - | |||||||||||||||||
We are making continuous progress in the field of plain bearings, including the practical use of composite materials and so
lid lubricants.
These are called Oilless bushings as no external lubrication is required. Oilless bearings have dry lubricant compressed into the base metal.
At the moment of frictional movement, particles of solid lubricants form tiny lubricating membranes on the surface of the moving part.
Viiplus Is The Market Leader For High End Aluminium Bronzes
Made To Order C954 Aluminium Bronze Bushing - "Made In China"
Aluminum bronze is the highest strength standard copper-based alloy.
Highest Strength Standard Size C95400 Aluminum Bronze Graphite Plugged Flange
Cast Bronze Sleeve Bushing for Excavators and Garbage trucks Bushing Bearings, Industrial robots bronze bushings, Injection molding machines bronze sleeve,
Shield tunneling machines bronze bushing Dam gates bronze bearings, Water turbine for Hydro power bronze bushings, Water valves bronze bushings and more.
High Quality Self Lubricating Bearings with Competitive Price.Quality China Products.SGS Audited Suppliers.Leading B2B Portal.
C95400 CuAl10Fe3 aluminum bronze is the most common aluminum bronze and is used in many heavy, high-load and high-wear locations.
Good tensile strength, ductility, weldability and fatigue resistance.
Typical applications include worm gears, bushings, pump components and bearings.
Aluminium bronze bushing C95400 Aluminum Bronze, also known by C954, is the most popular, all purpose aluminum bronze alloy.
It provides high yield and tensile strength, good ductility, weldability and exceptional resistance to wear, fatigue and deformation under shock or overload.
C95400 aluminum bronze is a tough, hard aluminum bronze that resists wear, abrasion and deformation under high compressive loads.
When combined with various metals, C95400 aluminum bronze extends the life of parts, lowers maintenance costs, reduces friction, scuffing and scuffing.
We produces C95400, C95500 and C95900 in standard sizes for rounds, tubes and rectangles. Aluminum, in conjunction with iron and nickel in C95500,
acts as a reinforcement in these alloys. All aluminum bronzes can be heat treated, which further increases the tensile strength.
| Copper Alloy No. | Cu% | Pb% | Sn% | Zn% | Fe% | P% | Ni% | Al% | Bi% | Mn% | S% | Sb% | Si% |
| C89325 | 84.00-88.00 | 0.1 | 9.00-11.00 | 1 | 0.15 | 0.1 | 1.003 | 0.005 | 2.70-3.70 | 0.08 | 0.5 | 0.005 | |
| C89831 | 87.00-91.00 | 0.1 | 2.70-3.70 | 2.00-4.00 | 0.3 | 0.05 | 1.003 | 0.005 | 2.70-3.70 | 0.08 | 0.25 | 0.005 | |
| C89833 | 86.00-91.00 | 0.09 | 4.00-6.00 | 2.00-6.00 | 0.3 | 0.05 | 1.003 | 0.005 | 1.70-2.70 | 0.08 | 0.25 | 0.005 | |
| C89835* | 85.00-89.00 | 0.09 | 6.00-7.50 | 2.00-4.00 | 0.2 | 0.1 | 1.003 | 0.005 | 1.70-2.70 | 0.08 | 0.35 | 0.005 | |
| C89844 | 83.00-86.00 | 0.2 | 3.00-5.00 | 7.00-10.00 | 0.3 | 0.05 | 1.003 | 0.005 | 2.00-4.00 | 0.08 | 0.25 | 0.005 | |
| C90300* | 86.00-89.001 | 0.3 | 7.50-9.00 | 3.00-5.00 | 0.2 | 0.052 | 1.003 | 0.005 | 0.05 | 0.2 | 0.005 | ||
| C90800 | 85.00-90.001 | 0.25 | 11.00-13.00 | 0.25 | 0.15 | 0.302 | 0.503 | 0.005 | 0.05 | 0.2 | 0.005 | ||
| C90810 | Rem.1 | 0.25 | 11.00-13.00 | 0.3 | 0.15 | 0.15-0.802 | 0.503 | 0.005 | 0.05 | 0.2 | 0.005 | ||
| C95400* | 83.00 min | 3.00-5.00 | 1.503 | 10.00-11.50 | 0.5 | ||||||||
| C95500* | 78.00 min | 3.00-5.00 | 3.00-5.503 | 10.00-11.50 | 3.5 | ||||||||
| C95900* | Rem. | 3.00-5.00 | 0.503 | 12.00-13.50 | 1.5 |
*Standard-stocked alloy. 1In determining Cu min., Cu may be calculated as Cu + Ni. 2For continuous castings, P shall be 1.5%, max.
3Ni value includes Co. Note: Unless otherwise noted, single values represent maximums.
| Tensile Strength (min) | Yield Strength (at .5% extention under load min) | Elongation (in 2in. or 50mm min, %) | Brinell Hardness (min) | ||
| Ksi | MPa | Ksi | MPa | ||
| 85 | 485 | 32 | 195 | 12 | 170 |
| Melting Point - Liquidus | 1038 °C |
| Melting Point - Solidus | 1027 °C |
| Density | 7.45 gm/cm3 at 20 °C |
| Specific Gravity | 7.45 |
| Electrical Conductivity | 0.075 MegaSiemens/cm at 20 °C |
| Thermal Conductivity | 58.7 W/m at 20 °C |
| Coefficient of Thermal Expansion 68-572 | 15.5 · 10-6 per °C (20-300 °C) |
| Specific Heat Capacity | 419 J/kg at 20 °C |
| Modulus of Elasticity in Tension | 107000 MPa |
| Magnetic Permeability* | 1.27 |
| Magnetic Permeability** | 1.2 |
Searching by bronze bushings material (product selector), You may select a bronze bearings material product and get a quote.
Manufacturer of continuous cast bronze C95400 Aluminum Bronze Bushings.
Viiplus metal polymer composite bearing bearings bushings products is the leading domestic china producer of plain bearings products and products.
Viiplus has excelled in the manufacturing of quality-crafted castings and metal products.
Thus, we have earned a reputation for meeting customer requirements for reliability,availability and value.
Aluminum bronze is the highest strength standard copper-based alloy. Suitable for high temperature environment to achieve self-lubrication.
VIIPLUS produces C95400, aluminum bronze bushing as standard-stocked bearings in standard sizes of sleeve bushes.
Aluminum in conjunction with iron and nickel in C954 acts as a strengthener in these alloys.
All of the aluminum bronzes bushing can be heat treated, further increasing tensile strengths.
✔ Standard-Stocked Bronze Sleeve Bushings With Graphite Product
Cast Bronze Bushings
C95400 Aluminum Bronze Bushing with graphite is a copper-based self-lubricating bearing for heavy load applications into which solid lubricant plugs are embedde.
C95400 Aluminum Bronze Bushing Features
Maintenance-free.
Excellent wear resistance in applications where oil film formation is difficult such as reciprocating, intermittent or oscillating motions under high loads and low speeds.
Low friction.
Range of operating temperatures.
Freedom of design on shape and the size.
The self-lubricating graphite plugged bronze sleeve bushings are machined from continuous cast bronze bar stock.
They are then milled and plugged with solid lubricant graphite based plugs.
Bronze Bushes
high-strength copper alloy as the base material, use conditions according to a certain proportion of its working surface machined hole and fill one solid lubricant.
High-strength copper alloy provides a high load carrying capacity and the solid lubricant can be formed lower friction. Under dry conditions we design ....
Flange Solid Bronze Metallic Self-lubricating Bearings
Copper Cast Bronze Bearings / Flanged Bronze Bearings
VSB-50 Flange Bronze Bushings
bearing bushing sleeve brass bearing sleeve brass sleeve bushing bushing sleeve
1. May work without any ol for long period
2. Extremely high load capacity, good anti-wear and lower friction
3. Particularly appropriate for low speed and high load
4. Suitable for reciprocating, oscillation or intermittent motion where oil film is hard to be formed
5. Good chemical resistant and anti-corrosion characteristics
6. Can b€ used in wide range of temperature from -40℃-+300℃
VSB-50 Flange material is made of strong cast bronze based metal with special solid lubricants embedded.
The base metal withstands high load and the solid lubricants provide self-lubrication.
The bearing shows excellent performance without pre-lubrication under conditions of extreme high/low temperature with low speed.
This material provides a maintenance-free bearing solution, particularly for high load, intermittent of oscillating motion.
| Grade | 50# | 50S1 | 50S2 | 50S3 | 650S5 |
| Material | CuZn25AI5Mn4Fe3 | CuSn5Pb5Zn5 | CuAI10Ni5Fe5 | CuSn12 | CuZn25AI5Mn4Fe3 |
| Density | 8 | 8.9 | 7.8 | 8.9 | 8 |
| Hardness | ≥210 | ≥70 | ≥150 | ≥75 | ≥235 |
| Tensile strength | ≥750 | ≥250 | ≥500 | ≥270 | ≥800 |
| Yield strength | ≥450 | ≥90 | ≥260 | ≥150 | ≥450 |
| Elongation | ≥12 | ≥13 | ≥10 | ≥5 | ≥8 |
| Coefficient o linear expansion | 1.9×10-5/℃ | 1.8×10-5/℃ | 1.6×10-5/℃ | 1.8×10-5/℃ | 1.9×10-5/℃ |
| Max.Temp. | -40~+300℃ | -40~+400℃ | -40~+400℃ | -40~+400℃ | -40~+300℃ |
| Max.dynamic load | 100 | 60 | 50 | 70 | 120 |
| Max.speed(Dry) | 15 | 10 | 20 | 10 | 15 |
| N/mm²*m/s(Lubrication) | 200 | 60 | 60 | 80 | 200 |
| Compression deformation | < 0.01 mm | < 0.05mm | < 0.04mm | < 0.05mm | < 0.005mm |
| Product NO. | Chemical Compositions | ||||||||
| VSB-50 | Cu | Zn | Al | Fe | Mn | Si | Ni | Sn | Pb |
| 60~66 | 22~28 | 5.0~8.0 | 2.0~4.0 | 2.5~5.0 | <0.1 | <0.5 | <0.2 | <0.2 | |
Bearing forms available in standard dimensions
· Cylindrical bushes
· Flanged bushes
· Sliding plates
Bearing forms made to order:
standard forms in special dimensions, thrust washers, flanged thrust washers, half-bearings, special shapes obtained by stamping or deep drawing, customized bearing designs
General industrial machinery and heavy industrial facilities.
Die/Mold Industry
We provide all kinds of self-lubricating sliding block, guide sleeve, wedge and other products for automobile tire mould, injection mould and stamping die.
Customer Bronze Bushings Size
Welcome to contact us!
The development of the VIIPLUS to study the new materials and new sliding bearings products
START YOUR PROJECTWITH AN APPLICATION ENGINEER
Sliding Bearing, Bimetal Bush, Wrapped Bronze Bushing, Oiles Bush, Oiles Bearing, Manufacturer China
Bushings,Lubricated Bearings,Composite Bearings,Metal Bearings,Compressor Bearings,Metal-polymer,Filament Wound,Plain Bearings,Flange Bearings,Polymer Bearings,Flange Bushings,Pump Bearings,Flanged Bushes,Thrust Plates,Industrial Bearing
FOLLOW US ON
https://www.bronzegleitlager.com
Designations And Information