Beryllium Copper Foil Strips CW101C (C17200) XHM State TM06 Mill Hardened Copper Strip
Product Normal Description:
Product Name: Beryllium copper foil strips
Grade: CW101C (C17200)
Standard: ASTM B194, SAE J463, J461
Product Specification: 0.1mmx250mm
State: XHM (TM06)
Typical Application: used for springs
Product Brand: CUBERYLLIUM®
CUBERYLLIUM ®-172 also named Cube2--UNS. C17200 (CDA 172) Beryllium Copper is the most commonly utilized Copper Beryllium alloy and is notable for its highest strength and hardness compared to commercial copper alloys. C17200 alloy contains appr. 2% of beryllium and achieves its ultimate tensile strength can exceed 1360Mpa, while the hardness approaches Rockwell C45. Meanwhile, the electrical conductivity is a minimum of 22% IACS in the fully aged condition.C17200 also exhibits exceptional resistance to stress relaxation at elevated temperatures.
Chemical Composition of Beryllium Copper CW101C (C17200) Alloy (CUBERYLLIUM ®-172):
Product Grade: CUBERYLLIUM ®-172(UNS. C17200)
Beryllium(Be): 1.80-2.00%
Cobalt(Co) + Nickel(Ni): 0.20% Min
Cobalt(Co) + Nickel(Ni) + Iron(Fe): 0.60% Max
Lead: 0.02% Max
Copper(Cu): Balance
Note: Copper plus additions equal 99.5% Minimum.
Typical Physical Properties of Beryllium Copper CW101C (C17200) Alloy(CUBERYLLIUM ®-172):
| Density (g/cm3): | 8.36 |
| Density before age hardening (g/cm3): | 8.25 |
| Elastic Modulus (kg/mm2 (103)): | 13.4 |
| Thermal Expansion Coefficient (20 °C to 200 °C m/m/°C): | 17 x 10-6 |
| Thermal Conductivity (cal/(cm-s-°C)): | 0.25 |
| Melting Range (°C): | 870-980 |
Temper Designations of Beryllium Copper Strips CW101C (C17200) (CUBERYLLIUM ®-172):
| Cuberyllium Designation | ASTM | Mechanical and Electrical Properties of Copper Beryllium Strip | ||||||
| Designation | Description | Tensile Strength (Mpa) | Yield Strength 0.2% offset | Elongation Percent | HARDNESS (HV) | HARDNESS Rockwell B or C Scale | Electrical Conductivity (% IACS) | |
| A | TB00 | Solution Annealed | 410～530 | 190～380 | 35~60 | <130 | 45~78HRB | 15～19 |
| 1/2 H | TD02 | Half Hard | 580～690 | 510～660 | 12~30 | 180~220 | 88~96HRB | 15～19 |
| H | TD04 | Hard | 680~830 | 620~800 | 2~18 | 220~240 | 96~102HRB | 15～19 |
| HM | TM04 | Mill hardened | 930～1040 | 750～940 | 9～20 | 270～325 | 28～35HRC | 17～28 |
| SHM | TM05 | 1030～1110 | 860～970 | 9～18 | 295～350 | 31～37HRC | 17～28 | |
| XHM | TM06 | 1060～1210 | 930～1180 | 4～15 | 300～360 | 32～38HRC | 17～28 | |
The Magor Applications of Beryllium Copper CW101C (C17200) (CUBERYLLIUM ®-172):
Product Photos:
FAQ:
Q1:Could you produce Beryllium Copper strip by Mill Hardened
process.
A1:Yes, we could produce AM(TM00), 1/2HM(TM01).HM(TM04) XHM(TM06)
XHMS(TM08).,we are the only factory could do harden strip in China.
Q2: What’s the advantages the Beryllium Copper of CUBERYLLIUM®.
A2: 1: The Biggest Coil weight could be reach 1200kg/Coil
2:We are the only one who melting by Vacuum semi-Continuous Furnace.
3:Surface further polishing for top clients.
Q3: Why you melting by Vacuum semi-Continuous Furnace.
A3:Could be get the Cast ingot without gas,smaller segregation,
Grain Refinement
Q4: What's the payment terms?
A4: We accept T/T, L/C, Paypal etc. It can be negotiated when the
amount is different.