Mining Industry Cement Mill Liners GX120Mn13 Wavy Liner Plates
Specification
1. Material:High Mn Steel
2. Hardness:HB190-230
3. Weight:52kg
4. Application:Mining Industry
5. MOQ:5tons
Product Photo
Technical Parameters
| Item | High Cr White Iron | High Cr Alloy Steel | High Mn Steel | Ni-hard Cast Iron |
| C | 2.4-3.2 | 1.1-2.2 | 0.9-1.3 | 2.4-3.6 |
| Si | 0.6-1.2 | 0.6-1.2 | ≤0.8 | ≤0.8 |
| Mn | 0.5-1.0 | 0.5-1.0 | 11.0-18.0 | ≤2.0 |
| Cr | 12.0-30.0 | 11.0-30.0 | 1.5-2.5 | 1.5-10 |
| S | ≤0.04 | ≤0.04 | ≤0.04 | ≤0.15 |
| P | ≤0.06 | ≤0.06 | ≤0.06 | ≤0.15 |
| Mo | 0.1-3.0 | 0.1-3.0 | ≤1.0 | ≤0.1 |
| Cu | 0.1-1.0 | 0.1-1.0 | - | - |
| Ni | 0-0.3 | 0-0.3 | - | 3.3-10 |
| Re | - | - | - | - |
| Equivalent Specification | GB/T8263-1999 AS2027 Cr27 AS2027 CrMo 15/3 AS2027 CrMo 20/2/1 ASTM A532 Class Ⅲ Type A 25%Cr ASTM A532 Class Ⅱ Type B 15%Cr-Mo BS 4844 3E DIN1695 NFA32401 | GB/T5680-1998 DL/T 681-1999 JIS G 5153-1999 ASTM A128 DIN GX120Mn12 AFNORZ120Mn12 | GB/T8263-1999 AS2027/Ni-Cr1-550 AS2027/Ni-Cr2-500 AS2027/Ni-Cr4-500 AS2027/Ni-Cr4-600 AS2027/Ni-Cr4-630 ASTM A532 1-A,B,C,D ASTM A532 2-A,B,C,D,E ASTM A532 3-A | |
| Material Type | Martensite Matrix | Austenitic Mn Steel | - | |
| Hardness | HRC≥56 | HB≤300 | HRC≥56 | |
| Impact Value | AK≥4J | AK≥80J | - | |
Production Facilities
1T,1.5T,3T,5T,12T,15T
Induction Electrical Furnace Heat Treatment Electrical Furnace
Inspection Facilities
Spectrometer Portable Hardness Tester
UT Test Electronic Metallographic Microscope
Our Services
We supply the following services:
1. Production of qualified wear and heat castings;
2. Design and installation of the boltless mill liners;
3. Consulting service of material selection of the mill liners under specific working condition to achieve
longer service life;
4. Consulting service of production & fineness improvement of grinding mills.
5.We can provide OEM/ODM for our clients.