asme sb408 astm B408 Nickel-Iron-Chromium Alloy Rod and Bar

ASTM B408 Nickel-Iron-Chromium Alloy Rod and Bar

nickel-iron-chromium alloys UNS N08120, UNS N08800, UNS N08810, UNS N08811, and UNS N08890 in the form of hot-worked and cold-worked rod and bar.

Alloy UNS N08800 is normally employed in service temperatures up to and including 1100°F (593°C). Alloys UNS N08120, UNS N08810, UNS N08811, and UNS N08890 are normally employed in service temperatures above 1100°F (593°C) where resistance to creep and rupture is required, and they are annealed to develop controlled grain size for optimum properties in this temperature range.

Nickel Alloy Bars - Nickel Alloy Rods - Nickel-Iron-Chromium Alloys

Chemical Requirements†

Element Composition Limits, %

Alloy N08120 Alloy N08800 Alloy N08810 Alloy N08811 Alloy N08890

Nickel 35.0 min 30.0 min 30.0 min 30.0 min 40.0 min

39.0 max 35.0 max 35.0 max 35.0 max 45.0 max

Chromium 23.0 min 19.0 min 19.0 min 19.0 min 23.5 min

27.0 max 23.0 max 23.0 max 23.0 max 28.5 max

Iron remainder 39.5 minA 39.5 minA 39.5 minA remainder

Manganese, max 1.5 1.5 1.5 1.5 1.5

Sulfur, max 0.03 0.015 0.015 0.015 0.015

Aluminum 0.40 max 0.15 min 0.15 min 0.15 min 0.05 min

... 0.60 max 0.60 max 0.60 max 0.60 max

Titanium 0.20 max 0.15 min 0.15 min 0.15 min 0.15 min

... 0.60 max 0.60 max 0.60 max 0.60 max

bar; rod; UNS N08120; UNS N08800; UNS N08801;

UNS N08810; UNS N08811; UNS N08890