Inconel 601/Alloy 601/Nickel 601/Uns N06601/W. Nr.
2.4851/Corrosion-Resistant Alloy/Super Alloy 601/Ncf601 Round Bar
Like Inconel 600, Inconel 601 has resistance to various forms of corrosion at high
temperature and oxidization. However Inconel 601 has an addition of
aluminum which give it high mechanical properties even in extremely
hot environments.
Inconel 601 is used for industrial furnaces, radiant tubes,
themocouple tubes, heat treatment equipments, baskets,
petrochemical process equipments and aircraft components.
Characteristic as below
1. Excellent inoxidability in the high temperature.
2. Good resistance to carbonizing.
3. Good inoxidabilitiy in sulfur atmosphere
4.Good mechanical property in both room temperature and high
temperature.
5.Good resistance to stress corrosion cracking, 601 have high creep
rupture strength since it limits
the carbon content and grain size, so recommend to use for above
500°C environment.
Inconel 601 Application field
1.The tray,basket and tool clamp in the heat treatment factory.
2.Steel shares at annealing and radiation control, high-speed gas
burners, Industrial furnace silk screen.
3.Separate tank of ammonia reforming and catalytic support grid of
nitric acid producing.
4.Exhaust system parts
5.Solid waste incinerator's combustion chamber
6.Channel support and soot dealing parts.
7.Detoxification exhaust system components
8.Oxygen re-heater
Chemical Composition
| Grade | Ni% | Mn% | Fe% | Si% | Cr% | C% | Cu% | Al% |
| Inconel 601 | 58-63 | Max 1.5 | Bal. | Max 0.50 | 21-25 | Max 0.10 | Max 1.00 | 1.0-1.7 |
Specifications
| Grade | Werkstoff Nr. | UNS |
| Inconel 601 | 2.4851 | N06601 |
Physical Properties
| Grade | Density | Melting Point |
| Inconel 601 | 8.1 g/cm3 | 1320°C-1411 °C |
Mechanical Properties
| Alloy State | Tensile Strength | Yield Strength | Elongation | Brinell Hardness (HB) |
| Annealing Treatment | 650 N/mm² | 300 N/mm² | 30% | – |
| Solution Treatment | 600 N/mm² | 240 N/mm² | 30% | ≤220 |
Our Production Standard
| Bar | Forging | Pipe | Sheet/Strip | Wire | |
| Standard | ASTM B166 | ASTM B166 | ASTM B167/B751/B755 | AMS B168 | ASTM B166 |
Surface Finishround bar
| Surface Finish | Definition and Application |
| No.1 | The surface is finished by heat treatment and pickling or processes corresponding theretoafter hot rolling |
| 2D | The finishes after cold rolling, by heat treatment, pickling or other equivalenttreatment |
| 2B | The finish after cold rolling, by heat treatment, pickling or other equivalent treatment and lastly by cold rolling to give an appropriate luster |
| BA | Cold rolled, bright annealed and skin-passed, the product have excellent brightness and good reflexivity like mirror |
| NO.3 | Polished with abrasive belt of grit#100~#200,have better brightness with discontinuous coarse stria |
| NO.4 | Polished with abrasive belt of grit#150~#180,have better brightness with discontinuous coarse stria |
| HL | Polished with abrasive belt of grit#150~#320 on the NO.4 finish and has continuous streaks |
| 8K | The product have excellent brightness and prefect reflexivity can be the mirror |