High Working Temperature Heating Element Wire/Strip 0.023 -0.8 Mm Thickness
Description
Fe-Cr-Al alloy wires are made of iron chromium aluminum base alloys
containing small amounts of reactive elements such as yttrium and
zirconium and produced by smelting, steel rolling, forging,
annealing, drawing, surface treatment, resistance control test,
etc.
With the characteristics of high resistance, low coefficient of
electric resistance, High operating temperature, good corrosion
resistance under high temperature.
It is mainly used in electric locomotive, diesel locomotive, metro
vehicle and high Speed moving car etc brake system brake resistor,
electric ceramic cooktop, industrial furnace.
Ribbon (flat wire)
Thickness: 0.023-0.8 mm (0.0009-0.031 inch)
Width: 0.038-4 mm (0.0015-0.157 inch)
Width/thickness ratio max 60, depending on alloy and tolerance
Other sizes are available on request.
Chemaical Composition and Main Properties
| Brand name | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
| Main chemical composition% | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 22.5-24.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.0 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
| RE | opportune amount | opportune amount | opportune amount | opportune amount | opportune amount | opportune amount | opportune amount | |
| Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
| Nb0.5 | Mo1.8-2.2 | |||||||
| Max.continuous service temp.of element (ºC) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
| Resistivity μΩ.m,20ºC | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
| Density (g/cm3 ) | 7.4 | 7.10 | 7.16 | 7.25 | 7.35 | 7.10 | 7.10 | |
| Thermal conductivity KJ/m.h.ºC | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | 45.2 | |
| Coefficient of lines expansion α×10-6/ºC | 15.4 | 16.0 | 14.7 | 15.0 | 13.5 | 16.0 | 16.0 | |
| Melting pointºC | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
| Tensile strength Mpa | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
| Elongation at rupture % | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
| Variation of area % | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
| Repeat bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
| Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
| Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
| Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | |
Features and advantages
1. High using temperature, the maximum using temperature can reach
1400C (0Cr21A16Nb, 0Cr27A17Mo2, etc.)
2. Low temperature coefficient of resistance
3. Lower thermal expansion coefficient than the Ni-base
super-alloys.
4. High electrical resistivity
5. Good corrosion resistance under high temperature, especially
under the atmosphere containing sulfides
6. High surface load
7. Creep-resistant
8. Lower raw-material cost, Lower density and cheaper price
compared with Nichrome wire.
9. Superior oxidation resistance at 800-1300ºC
10. Long service life
Application
Our products (FeCrAl) is widely used in Industry furnace, Home appliance like panel heaters, infrared
heaters, warming plates, air guns, hobby klins, radiators, grills,
industrial infrared dryers, in quartz tube heaters for space
heating, in ceramic heaters for cooking plates, toasters,
toasterovens, y etc