JB 8800 High Building Two Components Structural Silicone Sealant

JB 8800 is two parts, room temperature neutral cure silicone sealant. It has high performance specifications making it suitable for secondary seal insulating glazing.
Features

1. Structural capability.

2. Outstanding adhesion to a wide range of substrates including coated and reflective glass, aluminum and steel spacers and a variety of plastics.

3. The cured product exhibits excellent weathering characteristics and a high resistance to ultra-violet (UV) radiation heat and humidity.

4. High level of mechanical properties, high modulus.

5. Odorless and non-corrosive cure.

6. Outstanding resistant to ozone and ultra-violet (UV) radiation
BENEFITS

1. Outstanding adhesion to a wide range of substrates including coated and reflective glass, aluminum, steel spacers and a variety of plastics.

2. Structural capability as secondary sealant for insulating glass units used in structural glazing.
3. Low water absorptions.
4. Consistently non-slump, permitting automated glazing.
5. Excellent usable life stability.
6. Adjustable cure rate ranging form 30 to 50 minutes.
7. Non-corrosive by-product

PACKAGING
JB 8800 Insulating Sealant is available in
Standard Size:
Part A-190L
Part B-19L

COLORS
JB 8800 Structural Sealant is available for standard color:
Part A-White
Part B-Black
After Mixing: Black
PERFORMANCE DATA

Test Parameter	Unit	Result
As Supplied Tested at 23ºC and 50% RH
Specific Gravity	g/ml	1.03
Flow (sag or slump)	mm	<2.5
Snap Time	minute	40~60
Working Time	minute	10~20
As Cured-after 21 days at 23ºC and 50% RH
Durometer Hardness, Shore A	Points	40
Elongation, Ultimate	%	450
Tensile Strength, Ultimate	Mpa(psi)	2.5