Description:
This type of product is widely used in general welding material with the magnesium of 5% and a little of Titanium fine grains. And this product is of high toughness, good forgeability, and well anti-corrosiveness, Furthermore, this is a good choice for color-match in welding after anodic process.
The model ER5356 do not suggested to use in aluminum alloy workpiece which working temperature is over 65℃,thus will cause corrosion cracking in welded joints. You should strictly clean the oxide film on the edge of the workpiece and oil before welding, otherwise it will make bad weld produce and cause porosity, slag inclusion and other defects. Also you can use a plate to hold molten metal to ensure meld form.
Usage:
The argon arc welding of Aluminum & Magnesium alloy welding wires is used as the filler material, widely used in welding among Al-Mg-Si, Almasilalloy and Aluminium & Magnesium alloy, like: bicycles, aluminum scoter, etc. engine carriage, pressure vessel, armory processing, ship-building. space shuttle etc.
DIN EN ISO 18273 | S AL 5356 (AlMg 5Cr) |
Werkstoff-Nr. | 3.3556 |
AWS/ASME A 5.10 | ER 5356 |
Specification:
Chemical component(wt)/% |
Si | Fe | Cu | Mn | Mg | Cr | Zn | Ti | Be |
| Al | ||||
≤0.25 | ≤0.4 | ≤0.1 | 0.05~0.2 | 4.5~5.5 | 0.05~0.20 | ≤0.1 | 0.06~0.20 | ≤0.0003 | Rem. |
Characteristic |
Melting range | 1060 - 1175°F |
Electrical conductivity | 29%IACS(O)；27%IACS(H18) |
Density | 2.66g/mm3 |
Anti corrosion performance | A(Gen) A(SCC) |
The coefficient of thermal expansion (20 ℃ ~300 ℃) | 23.7×10-6/K |
Thermal conductivity (20 ℃) | 110-150W/m·K |
Wire standard:
GB10858-2008
ANSI/AWS A5.10-92
Passed ISO9001:2008 Quality Management System
The mechanical properties of the welding joints |
Motherboard | Motherboard performance | Joint properties | |||||
Rm (MPa) | RP0.2 (MPa) | A/% | Rm (MPa) | RP0.2 (MPa) | A/% | ||
6061-T6/T651 | 310 | 275 | 12 | 205 | 130 | 11 | |
6063-T6 | 240 | 210 | 12 | 135 | 80 | 12 | |
7005-T6/T63 | 370 | 315 | 12 | 315 | 205 | 10 | |
7039-T64 | 445 | 380 | 13 | 300 | 170 | 13 | |
5086-H32 | 290 | 205 | 12 | 265 | 115 | 17 | |
5083-O | 310 | 200 | 16 | 285 | 120 | 15 | |
6082-T6 | 310 | 275 | 11 | 210 | 130 | 10 | |
|
TIG (1000mm/5kg in plastic box/10kgCTNS)
MIG(0.5kg/2kg/7kg in plastic spool)