Breakage Resistance Tungsten Carbide Inserts With 100% Original Material
Custom Carbide Inserts Description
Tungsten Carbide Inserts Parameters
| No. | Grade | Grade description | Grade(Competitors) |
| 1 | YBC152 | CVD coated P10–P20 carbide grade for finishing to medium operation of steel and casting steel. Outstanding performance under higher cutting speed and temperature with excellent wear resistance. | GC4315(), E6020(MITSUBISHI), T9125(TUNGALOY) |
| 2 | YB6315 | CVD coating grade combining nano dioxygen gradient transition techniques and crystal nucleus pre-insertion techniques. | GC4315(), T9115(TUNGALOY) |
| 3 | YBC252 | CVD coated P20–P35 carbide grade for medium operation to roughing of steel and casting steel. Optimal performance of wear resistance and toughness for a wide application field. | GC4325(),E6020(MITSUBISHI),T9125(TUNGALOY) |
| 4 | YBD102 | CVD coated K05–K20 carbide substrate. Optimized for medium operation of cast iron, special nodular cast iron and hard steel at high cutting speed. | UC5115(MITSUBISHI) |
| 5 | YBD152 | CVD coated K10–K25 carbide substrate. Optimized for medium to roughing operation of cast iron. Good wear resistance and toughness at higher cutting speed. | UC5115(MITSUBISHI) |
| 6 | YBD152C | Thick Al2O3 CVD coated K05–K25 carbide substrate. Optimized for medium to roughing operation of cast iron.Higher wear resistance and toughness at higher cutting speed in combination with TC chip breaker. | UC5115(MITSUBISHI) |
| 7 | YB7315 | CVD coated K10–K25 carbide substrate. Optimized for medium to roughing operation of cast iron. Improved wear resistance and toughness at high cutting speed. | UC5115(MITSUBISHI), WAK20() |
| 8 | YBM153 | CVD coated M10–M25 carbide grade for fnishing to medium application in stainless steel. High wear resistance and capability against plasctic deformation at higher cutting speed. | |
| 9 | YBM253 | CVD coated M15–M35 carbide grade for medium to roughing operation in stainless steel with wide application field. High wear resistance and capability against plasctic deformation at higher cutting speed. | |
| 10 | YBG202 | PVD coated M10–M25/P10–P30 carbide substrate for finishing to medium application of stainless steel and steel (milling). Good wear resistance in a wide application field. | |
| 11 | YBG205 | PVD multilayer coated M20–M40/S15–S25/P10–P30 carbide substrate for finishing to medium application of stainless steel, super alloy and steel (milling). Good wear resistance and thermal stability in a wide application field. | VP15TF(MITSUBISHI) |
| 12 | YB9320 | PVD multilayer coated M10–M25/P10–P30 carbide substrate for finishing to medium application of stainless steel, super alloy and steel (grooving/milling).Optimized coating stability for higher wear resistance and thermal stability in a wide application field. | |
| 13 | YNT251 | Uncoated P10–P25 cermet grade for fine finishing to medium operation of steel and stainless steel. Good wear resistance and toughness. Suitable also in light interrupted cut. | |
| ... | ... | DON'T HESITATE TO CONTACT US TO GET MORE DETAILS! | ... |
YG3X 14.6-15.2 1320 92 is suitable for high speed finishing of small cutting sections of cast iron, non-ferrous metal and alloy quenched steel alloy steel.
YG6A 14.6-15.0 1370 91.5 is suitable for
semi-finishing of hard cast iron, non-ferrous metals and their
alloys, as well as semi-finishing and finishing of high manganese
steel, quenched steel and alloy steel.
The production and application of
YG6X 14.6-15.0 1420 91 show that the alloy has good effect in processing cold-hard alloy cast iron and heat-resistant alloy steel, and is also suitable for surface treatment of ordinary cast iron.
YG6 14.5-14.9 1380 89 is suitable for medium
cutting speed semi-finishing of cast iron, non-ferrous metal and
alloy non-metallic materials.
YG6X-1 14.6-15.0 1500 90 is suitable
for continuous cutting, semi-precision turning, small section
precision turning, rough turning thread, continuous section
semi-precision milling, hole roughing and precision milling of cast
iron, non-ferrous metal and its alloy non-metallic materials.
YG8N 14.5-14.8 2000 90 is suitable for
high speed cutting of cast iron, white cast iron, nodular cast
iron, chromium, nickel stainless steel and other alloy materials.
YT5 12.5-13.2 1430 89.5 is suitable for rough
turning, rough shaving, semi-fine shaving, rough grinding and
drilling of discontinuous surfaces of carbon and alloy steels
(including steel forgings, stamping parts and casting surfaces).
YS25 12.8-13.2 2000 91 is suitable for
rough turning, milling and planing of carbon steel, cast steel,
high manganese steel, high strength steel and alloy steel.
YT14 11.2-12.0 1270 90.5 is suitable for rough
turning, rough turning and continuous cutting in the processing of
carbon steel and alloy steel, semi-finish turning and precision
turning in intermittent cutting, continuous rough turning, drilling
and rough expansion of casting holes.
| TYPE | ΦI.C | S | Φd | |||
| RDKW0702MO | 7 | 2.38 | 2.8 | |||
| RDKW0803MO | 8 | 3.18 | 3.4 | |||
| RDKW10T3MO | 10 | 3.97 | 4.4 | |||
| RDKW1204MO | 12 | 4.76 | 4.4 | |||
| RDKW1605MO | 16 | 5.56 | 5.5 | |||
| RDKW2006MO | 20 | 6.35 | 6.5 | |||
| TYPE | ΦI.C | S | Φd | |||
| RCKT10T3MO-DM | 10 | 3.97 | 4.4 | |||
| RCKT1204MO-DM | 12 | 4.76 | 4 | |||
| RCKT1606MO-DM | 16 | 6.35 | 5.56 | |||
| TYPE | ΦI.C | S | Φd | |||
| RCKT1206MO-DR | 10 | 3.97 | 4.4 | |||
| RCKT1606MO-DR | 12 | 4.76 | 4 | |||
| RCKT2006MO-DR | 16 | 6.35 | 5.56 | |||