ASTM A335 Seamless ferritic and alloy steel pipe for high temperature service
Key words: ASTM A335 P91 A335 P22 material composition A335 P22 Pipe P9
Chemical composition
Alloy steel pipe, High temperature service,Seamless steel pipe,Steel pipe,Temperature service application.
Applications: For Boilers,Superheaters,Heat-Exchangers
Size range: O.D.:6-168mm W.T.:1-15mm L: according to customer requirement
Kindly advise.
Transverse or Longitudinal Tensile Test and Flattening Test,Hardness Test or Bend tests.
| Steel Grade and Chemical Compositions: | |||||||
| Steel Grade | C | Mn | P | S | Si | Cr | Mo |
| max | max | max | max | max | min | ||
| P5 | 0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.50 | 4.00-6.00 | 0.45-0.65 |
| P9 | 0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.25-1.00 | 8.00-10.00 | 0.90-1.10 |
| P11 | 0.05-0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.50-1.00 | 1.00-1.50 | 0.44-0.65 |
| P12 | 0.05-0.15 | 0.30-0.61 | 0.025 | 0.025 | 0.50 | 0.80-1.25 | 0.44-0.65 |
| P21 | 0.05-0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.50 | 2.65-3.35 | 0.80-1.06 |
| P22 | 0.05-0.15 | 0.30-0.60 | 0.025 | 0.025 | 0.50 | 1.90-2.60 | 0.87-1.13 |
| P91 | 0.08-0.12 | 0.30-0.60 | 0.020 | 0.010 | 0.20-0.50 | 8.00-9.50 | 0.85-1.05 |
| P92 | 0.07-0.13 | 0.30-0.60 | 0.020 | 0.010 | 0.50 | 8.50-9.50 | 0.30-0.60 |
| Steel Grade | Tensile Strength | Yield Strength | Elongation | Hardness.Max | ||
| min.ksi [Mpa] | min.ksi [Mpa] | % | Brinell/Vickers | Rockwell | ||
| P1, P2 | 55[380] | 30[205] | 20 | |||
| P12 | 60[415] | 32[220] | 20 | |||
| P23 | 74[510] | 58[400] | 20 | |||
| P91 | 85[585] | 60[415] | 30 | 250 HB/265 HV | 25 HRC | |
| P92, P911 | 90[620] | 64[440] | 30 | 250 HB/265 HV | 25 HRC | |
| P122 | 90[620] | 58[400] | 30 | 250 HB/265 HV | 25 HRC | |