ASTM F67 F136 Medical Dental Titanium Alloy Disc Instock Pure Titanium Disc For Dental Implants, Crowns, Bridges
| BaseTi - Dental Pure Titanium Disc Inventory | ||
| Grade | Stock Size | Weight(kg) |
| ASTM Grade 2 ASTM Grade 3 | Φ98mm*10mm | 0.34 |
| Φ98mm*12mm | 0.41 | |
| Φ98mm*14mm | 0.48 | |
| Φ98mm*16mm | 0.54 | |
| Φ98mm*18mm | 0.61 | |
| Φ98mm*20mm | 0.68 | |
| Φ98mm*22mm | 0.75 | |
| Φ98mm*24mm | 0.82 | |
| Φ98mm*25mm | 0.85 | |
| BaseTi - Dental Titanium Alloy Disc Inventory | ||
| Grade | Stock Size | Weight(kg) |
| ASTM Grade 5 Ti-6Al-4V | Φ98mm*10mm | 0.34 |
| Φ98mm*12mm | 0.41 | |
| Φ98mm*14mm | 0.48 | |
| Φ98mm*16mm | 0.54 | |
| Φ98mm*18mm | 0.61 | |
| Φ98mm*20mm | 0.68 | |
| Φ98mm*22mm | 0.75 | |
| Φ98mm*24mm | 0.82 | |
| Φ98mm*25mm | 0.85 | |
*The dimensions listed in the table above represent the sizes we regularly supply, and we have ample stock available. *Should you require customized dimensions for your titanium discs, or specific tolerance parameters, we are able to complete production within a swift timeframe of 10 to 15 days. | ||
BaseTi Unveils Ultimate Guide for Dental Titanium Discs Across Various ASTM Grades
New York, NY – Today, BaseTi, a leading titanium manufacturer and
supplier, has released an informative guide targeting international
buyers in the dental sector.
Why It Matters
As dental technology advances, the materials used are pivotal for
successful outcomes. Dental Titanium Discs are gaining momentum for
their blend of durability and biocompatibility. BaseTi's new guide
demystifies the various ASTM Grades and how they cater to different
dental applications.
The Breakdown on Grades
Navigating the maze of material grades can be overwhelming,
especially when compliance with international standards such as
ASTM F67, ASTM F136, and EN ISO 5832 is essential.
ASTM Grade 2: The Ideal Choice for Dental Crowns and Bridges
Comprised of pure titanium, ASTM Grade 2 conforms to ASTM F67 and
EN ISO 5832-2. It is the material of choice for crafting dental
crowns and bridges.
ASTM Grade 3: Perfect for Implant Abutments
A notch above Grade 2, this higher-grade pure titanium is in line
with ASTM F67 and EN ISO 5832-2. It is most suited for crafting
implant abutments and metal frameworks.
ASTM Grade 5: The Go-To for High-Stress Implants
Also known as Ti6Al4V, this titanium alloy is standardized under
ASTM F136 and EN ISO 5832-3. It is engineered for high-stress
implants and complex orthodontic devices.
Special Spotlight on BaseTi
BaseTi, the titanium factory, not only serves as a supplier but as
an innovator in the field. Their range includes Pure Titanium
Dental Discs, Dental Ti Discs, Titanium Dental Milling Discs, and
even Dental Implant Discs.
What’s Next?
Understanding the various grades and their dental applications is
made simpler with BaseTi's new guide. Whether it's dental crowns,
implant abutments, or advanced orthodontic equipment, BaseTi has
you covered.
About BaseTi
As a trusted titanium manufacturer, BaseTi offers a wide range of
Dental Titanium Alloy Discs to meet the diversified needs of the
dental industry. Their commitment to quality and compliance makes
them a preferred choice for international buyers.
Attribute | ASTM Grade 2 | ASTM Grade 3 | ASTM Grade 5 |
|---|---|---|---|
U.S. Standards | ASTM F67 | ASTM F67 | ASTM F136 |
European Standards | EN ISO 5832-2 | EN ISO 5832-2 | EN ISO 5832-3 |
Material | Pure Titanium | Pure Titanium (more alloyed than Grade 2) | Titanium Alloy (Ti6Al4V) |
Applications | Dental crowns, bridges | Dental implants, abutments | High-load-bearing implants, complex dental prosthetics |
Specific Products | Dental Crowns and Bridges, Less-load-bearing dental implants | Dental Implants and Abutments, more load-bearing compared to Grade 2 | Complex Dental Prosthetics, High-load-bearing dental implants |
The physical properties of dental titanium discs vary depending on the grade of the material and the respective standards they meet. Below is a comprehensive table that encapsulates these vital features:
| Attribute | ASTM F67 (U.S.) | ASTM F136 (U.S.) | EN ISO 5832-2 (EU) | EN ISO 5832-3 (EU) |
|---|---|---|---|---|
| Grade | Grade 2 | Grade 5 | Grade 2 | Grade 5 |
| Density (g/cm³) | 4.51 | 4.43 | 4.51 | 4.43 |
| Tensile Strength (MPa) | 345-450 | 930-1030 | 345-450 | 930-1030 |
| Yield Strength (MPa) | 275-450 | 860-880 | 275-450 | 860-880 |
| Elongation (%) | 20 | 10-16 | 20 | 10-16 |
| Hardness (HV) | 120-180 | 350-440 | 120-180 | 350-440 |
Element | ASTM F67Grade 2 (%) | ASTM F136 Grade 5 (%) | EN ISO 5832-2 Grade 2 (%) | EN ISO 5832-3 Grade 5 (%) |
|---|---|---|---|---|
C | ≤ 0.10 | ≤ 0.08 | ≤ 0.10 | ≤ 0.08 |
O | ≤ 0.25 | ≤ 0.20 | ≤ 0.25 | ≤ 0.20 |
N | ≤ 0.03 | ≤ 0.05 | ≤ 0.03 | ≤ 0.05 |
H | ≤ 0.015 | ≤ 0.012 | ≤ 0.015 | ≤ 0.012 |
Fe | ≤ 0.30 | ≤ 0.25 | ≤ 0.30 | ≤ 0.25 |
Al | -- | 5.5-6.75 | -- | 5.5-6.75 |
V | -- | 3.5-4.5 | -- | 3.5-4.5 |