RAL2005 Luminous orange electrostatic thermoset powder coating for Electrical appliances
Proper surface preparation is paramount. Inadequate surface preparation leads to poor adhesion, coating defects, and premature failure of the coating system. Per NAVSEA Standard Item (NSI) 009-32, a near white metal blast (NACE 2/SSPC-SP 10) is required. Surface preparation by chemical treatment requires approval by NAVSEA. Powder coatings are applied by fluidized bed, electrostatic spray, or flocking. Fluidized bed and electrostatic spray are the most common methods.
The fluidized bed method involves the use of a large tank or chamber that holds the powder. Dry air is circulated through the powder, giving it a fluid-like texture. The preheated component is dipped into the fluidized powder. The powder melts on contact with the heated surface to form a continuous coating. The fluidized bed is generally used for very thick applications (10–30 mils).
Physical Properties
| TP-1 | TP-2 | ||||
|---|---|---|---|---|---|
| Flexibility | BS3900 E1 | Pass | mm | 6 | 5 |
| Scratch | BS3900 E2 | Pass | kg | 4 | 4 |
| Impact | BS1391 | ||||
| Direct | Pass | in lbs | 80 | 100 | |
| Reverse | Pass | in lbs | 80 | 100 | |
| Erichsen Cupping | BS3900 E4 | Pass | mm | 6 | 8 |
| Cross Hatch | BS3900 E6 | Pass | % | 100 | 10 |
For specific confirmation of any details in the product information or use and application please apply to the company in writing.
Household appliances.
Automotive parts.
Bicycle components.
Coating of aluminum extrusions.
Window trims.
Agricultural equipment.
Aerospace areas.
Interior and exterior furniture.
Architecture construction.
Metal fence and rails.
Food service areas.
Goods display, etc.
| Testing Items | Standard | Data |
| Appearance | Flat And Smooth | |
| Coating Thickness | GB/T6554-2003 | 50~70mm |
| Gloss(60°) | GB/T9754-2007 | From 2%~100% to All Gloss |
| Impact Resistance | GB/T1732-1993 | 50kg.cm |
| Bending Performance | GB/T6742-2007 | 2mm |
| Cupping | GB/T9753-2007 | 8mm |
| Adhesion Force | GB/T9286-1998 | 0 Grade |
| Hardness | GB/T6739-2006 | 2H |
Resistant to Salt (1000 Hours) | GB/T1771-2007 | No Change For Coating Appearance |
| Humidity And Heat Resistance (1000 Hours) | GB/T1740-2007 | No Change For Coating Appearance |
Chemical Medium Resistance (240 Hours) 5%H2SO4 5%HCl 5%NaOH 5%NaCl | GB/T1763-1979 |
No Change For Coating Appearance No Change For Coating Appearance No Change For Coating Appearance No Change For Coating Appearance |
| Heat Resistance | GB/T1735-2009 | It Can Reach Between 220℃/20minutes And 240℃/40minutes According To Color And Different Requirement |