OD 5mm High Temperature Cable Material 0Cr25Al5 Resistance Wire
1. Introduction
High temperature heating wires are used for making electric heating elements in home appliances and industrial furnaces.
2. parameters
| Alloy Type | Diameter (mm) | Resistivity (μΩm)(20°C) | Tensile Strength (N/mm²) | Elongation(%) | Bending Times | Max.Continuous Service Temperature(°C) | Working Life (hours) |
| Cr20Ni80 | <0.50 | 1.09±0.05 | 850-950 | >20 | >9 | 1200 | >20000 |
| 0.50-3.0 | 1.13±0.05 | 850-950 | >20 | >9 | 1200 | >20000 | |
| >3.0 | 1.14±0.05 | 850-950 | >20 | >9 | 1200 | >20000 | |
| Cr30Ni70 | <0.50 | 1.18±0.05 | 850-950 | >20 | >9 | 1250 | >20000 |
| ≥0.50 | 1.20±0.05 | 850-950 | >20 | >9 | 1250 | >20000 | |
| Cr15Ni60 | <0.50 | 1.12±0.05 | 850-950 | >20 | >9 | 1125 | >20000 |
| ≥0.50 | 1.15±0.05 | 850-950 | >20 | >9 | 1125 | >20000 | |
| Cr20Ni35 | <0.50 | 1.04±0.05 | 850-950 | >20 | >9 | 1100 | >18000 |
| ≥0.50 | 1.06±0.05 | 850-950 | >20 | >9 | 1100 | >18000 | |
| 1Cr13Al4 | 0.03-12.0 | 1.25±0.08 | 588-735 | >16 | >6 | 950 | >10000 |
| 0Cr15Al5 | 1.25±0.08 | 588-735 | >16 | >6 | 1000 | >10000 | |
| 0Cr25Al5 | 1.42±0.07 | 634-784 | >12 | >5 | 1300 | >8000 | |
| 0Cr23Al5 | 1.35±0.06 | 634-784 | >12 | >5 | 1250 | >8000 | |
| 0Cr21Al6 | 1.42±0.07 | 634-784 | >12 | >5 | 1300 | >8000 | |
| 1Cr20Al3 | 1.23±0.06 | 634-784 | >12 | >5 | 1100 | >8000 | |
| 0Cr21Al6Nb | 1.45±0.07 | 634-784 | >12 | >5 | 1350 | >8000 | |
| 0Cr27Al7Mo2 | 0.03-12.0 | 1.53±0.07 | 686-784 | >12 | >5 | 1400 | >8000 |
| NAME | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 | |
| MAIN CHEMICAL | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 22.5-24.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.0 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 | |
| COMPOSITION | Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune |
| Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest | |
| Nb0.5 | Mo1.8-2.2 | |||||||
| MAX TEMPERATURE(oC) | 650 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 | |
| RESISTANCE20oC (μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 | |
| DENSITY(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 | |
| HEAT EXCHANGE | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | 45.2 | |
| RATE(KJ/m·h·oC) | ||||||||
| expansion rate(α×10-6/oC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 | |
| melting point( oC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 | |
| tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 | |
| elongation(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 | |
| variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 | |
| bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 | |
| hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | |
| micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | |
| magnetic property | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | |
3. Characteristics
1) Excellent straightness
2) High strength in high temperature
3) Uniform and beautiful surface condition without spots
4) Good corrosion resistance
4. Applications
1) This wire can also be widely used in generally specified for transistor caps, anodes for electronic tubes,
leads of electronic components / lead-in-wires for lamps and for wire-mesh. Also used in strip form for various applications including Ni-Cd batteries
2) Also used for cables, Lead-in-Wire for lamps, electronic tube supports, wire cloth electrical connecting leads where temperatures are in excess of those for which copper is suitable, wire weaving
3) Typical applications include: terminations for heating elements as in ovens, plastics extruders, furnaces. Filament supports and lead wires in the lighting industry