GUANGDONG NEW ERA COMPOSITE MATERIAL CO., LTD. |
|
Verified Suppliers
|
|
|
27 Mic Book Laminating Film , Book Protection Film For Luxury Catalogue Lamination
Glossy Specifications:
TYPE | THICKNESS (micron) | ||
GLOSSY | TOTAL | BASE | EVA |
17 | 12 | 5 | |
18 | 12 | 6 | |
20 | 12 | 8 | |
22 | 12 | 10 | |
23 | 15 | 8 | |
25 | 15 | 10 | |
27 | 15 | 12 | |
30 | 15 | 15 | |
42 | 28 | 14 | |
WIDTH (mm) | 200 ~ 2210 | ||
LENGTH (m) | 100 ~ 8000 | ||
PAPER CORE | 25.4mm(1 inch) / 76mm (3 inch) | ||
BONDING | ≤2 | ||
CORONA TREATED | Double side | ||
SURFACE TENSION | 38 Dyne/cm ≤ 42 Dyne/cm | ||
LAMINATION TEMP. | 90±10°C | ||
ROLLER PRESSURE | 10 ~ 20Mpa | ||
LAMINATION SPEED | 20 ~ 70M | ||
Matte Specifications:
| TYPE | THICKNESS (micron) | ||
| MATTE | TOTAL | BASE | EVA |
| 17 | 12 | 5 | |
| 18 | 12 | 6 | |
| 20 | 12 | 8 | |
| 22 | 12 | 10 | |
| 23 | 15 | 8 | |
| 25 | 15 | 10 | |
| 27 | 15 | 12 | |
| 30 | 15 | 15 | |
| 43 | 28 | 15 | |
| WIDTH (mm) | 200 ~ 2210 | ||
| LENGTH (m) | 100 ~ 8000 | ||
| PAPER CORE | 25.4mm(1 inch) / 76mm (3 inch) | ||
| BONDING | ≤2 | ||
| CORONA TREATED | Double side | ||
| SURFACE TENSION | 38 Dyne/cm ≤ 42 Dyne/cm | ||
| LAMINATION TEMP. | 90±10°C | ||
| ROLLER PRESSURE | 10 ~ 20Mpa | ||
| LAMINATION SPEED | 20 ~ 70M | ||
Description:
Thermal Lamination Films have extrusion-coated surface with low temperature melting resin, which enables the lamination of film to paper products by heat and pressure. Various surface finishes available add value to the printed surface.
Glossy BOPP thermal lamination film offers a shiny colorful finish. Its use can enhance the look and increase all laminated presswork’s useful lifetime. Matt BOPP thermal lamination film provides a matt-finish on the surface of presswork, protecting from fingerprints and smudges. Compared with gloss thermal lamination film, matt film can be preserved for longer period of time.
A combination of good performance characteristics and low price point make BOPP thermal laminating films ideal for all kinds of printed & unprinted paper and paper boards, including book covers, cosmetics packaging, magazines, documents, shopping bags, Diaries etc.
Why chooses NEI BOPP thermal laminating film for book lamination?
1. Environmentally friendly: It is non-toxic, odorless, or non-benzene because non-solvent based adhesive is used. It is environmentally friendly and non-hazardous to human health since no toxic gases or volatile content is emitted during lamination process. In addition, it is easier to recycle than water-based lamination film because film and paper can be easily separated.
2. Safe operation: Non-solvent based adhesive is used so it will
eliminate the fire hazard that is caused by the use and storage of
flammable solvents.
3. Excellent performance: Compared with wet lamination, thermal
lamination film enhances the color saturation and brightness of
presswork. It also has stronger ability of absorbing powder and
adhesive force. Furthermore, it is effective to prevent being
blistered or separated from presswork in lamination process. As it
has strong adhesive ability and surface tension, it can be used for
latter processes, including spot UV, hot stamping, die cutting,
indentation process.
4. Easy handling
5. High efficiency
6. Wide adaptability
Why chooses NEI?
1. NEI has professional experience in film industry since 1995 so we have good quality control and after-sale services to support you.
2. 10 yeas of export experience to many countries, including South America, North America, Middle East, Asia, Africa, Oceania, etc.
3. Compared with other thermal lamination film, our EVA glue is 100% imported from Korea and it ensures the adhesiveness of our film.
4. Customize size and thickness according to customer requests. Labels can be customized as well.
5. Rapid production and delivery.
Special Instruction:
1. NEI BOPP thermal lamination film is suggested to be laminated with the roller temperature range of 85 to 110°C and roller pressure of 10 to 20 Mpa. However, the optimum conditions are depending on the selected laminator’s speed and dimensional stability.
2. It is advised that the printed surface is well dried before lamination and cools sufficiently one surface before laminating to other surface.