Ixpe Foam Expanded Polyolefin Foam Cross Linked Polyethylene Foam Density
Electronic cross-linked polyethylene foam also named Physical
crosslinked polyethyele foam, Irradiation crosslinked polyethylene
foam.Common abbreviations IXPE foam, IXLPE foam.It is made of
low-density polyethylene (LDPE), AC foaming agent and other powders
after being melted, mixed and extruded, and then foamed at high
temperature. IXPE has finer cells, smoother surface and better
mechanical properties than XPE.
Production process: compounding-extrusion-irradiation-foaming.
Note: IXPE foam can be made anti-static (we will talk about
anti-static IXPE later), but XPE cannot (theoretically it is
possible, but our company does not currently produce).
Specifications
| ||||
| Property | Standard | Unit | Value | |
| Density | - | Kg/m³ | 50.00 | |
| Tensile Strength | Transverse | ISO-1798 | MPa | 0.33~0.36 |
| Longitudinal | 0.48~0.50 | |||
| Elongation | Transverse | ISO-1798 | % | 95.20~102.10 |
| Longitudinal | 100.20~109.10 | |||
| Tearing Strength | Transverse | ISO-8067
| Kn/m | 1.97~2.14 |
| Longitudinal | 2.48~2.71 | |||
| Compression 25% | ISO-3386-1 | kPa | 58.00 | |
| Compression 40% | ISO-3386-1 | kPa | 95.60 | |
| Compression 50% | ISO-3386-1 | kPa | 132.00 | |
| Compression Set 25% 0.5H | ISO-1856 | % | 13.22 | |
| Compression Set 25% 24H | ISO-1856 | % | 4.68 | |
| Operating Temperature Range | Internal | °C | (-40,+80) | |
| Water Absorption % Volume (Maximum) | Internal | % | 0.40 | |
| Thermal Conductivity | JIS A1412-2 | W/mK | 0.055 | |
| Shore - C | ASTM D2240 | °C | 30 | |
| Flammability | FMVSS302 | mm/min | - | |
Additional Information
● All tests were carried out in 23°C ± 2.
● Data represents typical values measured on a 4mm thick specimen and should be considered as guidelines only.
The said product is a close-cell, conductive foam. It is produced by compounding the PE resin with conductive fillers &
blowing agents to extrude certain sheets,then cross-linking and foaming. The basic process can be summarized to the following:
1 Pellitizing master batch by compounding PE resin with carbon
black and AC foaming agents;
2 Extrude the said batch to make certain sheets with different
thickness & width;
3 Cross link the said sheets under electric beam;
4 Make the cross linked sheets foam in foaming furnace
Characteristics
1. Light weight, good elasticity
2. Weatherproof and waterproof
3. Flame retardant
4. Sound absorption
5. Heat insulation
6. Elastic and flexibility
Features
1. Light weight, good elasticity
2. Weatherproof and waterproof
3. Flame retardant
4. Sound absorption
5. Heat insulation
6. Thermal insulation
7. Elastic and flexibility
8. Shock absorption
Qur services
Factory direct selling with competitve price, sooner
leadtime,better customized services.
Samples in stock can be arranged in one working day.
Company info
CYG TEFA is the earliest PE foam manufacturing with scale
production in China since 2002.Mainly produce XPE FOAM,IXPE
FOAM,IXPP FOAM and ESD PRODUCT(Foam type: PE/EVA/PU/EPE/PP
Plastic).Annual production capacity is about 6000 tons.2 bases one
in Shen zhen and an other in Huzhou,with total 17 production
lines.CYG Management control system: Kingdee / OA / Oracle.CYG have
a professional team and technology.More than 30 R&D
staff.Through the great variety of our products we provide people
with a warm and quiet home and working environment.
IXPP project (three years: Proposal stage - Develop - Sampling - Approved product- Small quantity supply for testing
11 employee
Investment rate: 4% to 10%
Responsible for : Improving available product / Technology
improving / New product development / New devices