Product Introduction:
Polyamide 66 GF25, dry impact resistent (PA 66), used for a variety of applications for thermal insulation in aluminum windows, doors and facade systems, polyamide (PA) offers good insulating properties and excellent mechanical performance.
Reinforced with glass fibers, the special PA 66 GF25, dry impact resistant mixture offers the best solution for aluminum systems for optimum results.
Features:
1. It has excellent mechanical properties, high strength, high toughness.
2. The material has excellent coloring ability, can achieve various requirements of color matching
3. The shrinkage rate of PA66 is between 1% and 2%. The addition of glass fiber additives can reduce the shrinkage rate to 0.2%~1%. The shrinkage ratio is large in the flow direction and in the direction perpendicular to the flow direction.
4. PA66 is resistant to many solvents, but is less resistant to acids and other chlorinating agents.
5. PA66 excellent flame retardant performance, by adding different flame retardants can achieve different levels of flame retardant effect.
Details of related standard:
Polywell PA66 Granules Performance Table
| NO. | Item | Unit | GB/T 23615.1-2009 | pw-Technical specification |
| Material Properties | ||||
| 1 | Density | g/cm3 | 1.3±0.05 | 1.28-1.35 |
| 2 | Linear expansion coefficient | K-1 | (2.3-3.5)*10-5 | (2.3-3.5)*10-5 |
| 3 | Vicat softening temperature | ºC | ≥230ºC | ≥233ºC |
| 4 | Melting point | ºC | ≥240 | ≥240 |
| 5 | Testing for tensile cracks | - | No cracks | No cracks |
| 6 | Shore hardness | - | 80±5 | 80-85 |
| 7 | Impact strength(Unnotched) | KJ/m2 | ≥35 | ≥38 |
| 8 | Tensile strength(longitudinal) | MPa | ≥80a | ≥82a |
| 9 | Elasticity modulus | MPa | ≥4500 | ≥4550 |
| 10 | Elongation at break | % | ≥2.5 | ≥2.6 |
| 11 | Tensile strength(transverse) | MPa | ≥70a | ≥70a |
| 12 | High temperature tensile strength(transverse) | MPa | ≥45a | ≥47a |
| 13 | Low temperature tensile strength(transverse) | MPa | ≥80a | ≥81a |
| 14 | Water resistance tensile strength(transverse) | MPa | ≥35a | ≥35a |
| 15 | Aging resistance tensile strength(transverse) | MPa | ≥50a | ≥50a |
1. Sample water content less than 0.2% by weight.
2. Norm laboratory condition:(23±2)ºC and (50±10)% relative
humidity.
3. The specifications marked with "a" only applies to I-shape strip
otherwise, the specifications concluded between supplier and buyer
through consultation, shall be written in contract or purchase
order.
Application:
It is mainly used for nylon extruding profiles and nylon thermal
break extruding strips. The granules produced by our company are
special materials for nylon extruding profiles.There are different
formulations for different shapes and complexities to ensure the
smooth production of nylon profiles.
Packaging & Delivery:
Packaging details:25kg/bag
Delivery details: shipped in 5-10 working days after receiving the payment
Our Company
Zhangjiagang Polywell Engineering Plastics Company is located in the city of Zhangjiagang, Jiangsu Province, China. Our company has devoted more than ten years to the research and development and production of nylon extruding profiles. According to customer reaction, using our PA66 granules for production can get high yiedl, easy start-up, and get less scrap in the early start-up stage. There will be no lack or incomplete of profiles in the production process, thus avoiding material waste.
Contact us:
Lana Lou
E-mail: lana@szpolywell.cn
Phone: 0086-13812855067 (WhatsApp)
Address:Jinfeng Town, Zhangjiagang City, Jiangsu Province, China