Thermal insulating profiles made of polyamide PA 66 GF25 have significant advantages.
1. The coefficient of linear thermal expansion (linear elongation coefficient) of the polyamide profiles is equivalent to the aluminum profile. Therefore, the polyamide profile is not subjected to internal stresses after it is pressed to aluminum profile. This is one of the most important advantages of using the polyamide material as a thermal barrier.
2. The deflection temperature of the polyamide profiles under load is high. Even at 200° C for about 15 minutes, no deformation occurs. Therefore, it can easily be heated in the ovens at the powder coating process.
3. Polyamide profiles do not emit toxic gases in case of fire. They are environmentally friendly.
The shape C thermal barrier polyamide strip can prevent the window
frame from dust and water, has a better mechanical performance, is
the first generation and easiest shape of insulating strips.
For the shape C, we can provide the following size or customize
according to customers' requirements.
high quality, competitive price, free sample support and short lead time, high mechanical strength, high toughness, high softening point, good wear resistance, self-lubrication, long-term work at higher temperatures, high CTI value, excellent electrical insulation, low smoke and toxicity characteristics.
It is mainly used in insulation broken bridge aluminium products, helping to reduce heat loss or heat gain through the aluminum, and has better performance in terms of power usage.
| Item | Unit | GB/T 23615.1-2009 | PW-Technical specification |
| Density | g/cm3 | 1.3±0.05 | 1.28-1.35 |
| Linear expansion coefficient | K-1 | (2.3-3.5)×10-5 | (2.3-3.5)×10-5 |
| Vicat softening temperature | ºC | ≥230ºC | ≥233ºC |
| Melting point | ºC | ≥240 | ≥240 |
| Testing for tensile cracks | - | No cracks | No cracks |
| Shore hardness | - | 80±5 | 80-85 |
| Impact strength(Unnotched) | KJ/m2 | ≥35 | ≥38 |
| Tensile strength(longitudinal) | MPa | ≥80a | ≥82a |
| Elasticity modulus | MPa | ≥4500 | ≥4550 |
| Elongation at break | % | ≥2.5 | ≥2.6 |
| Tensile strength(transverse) | MPa | ≥70a | ≥70a |
| High temperature tensile strength(transverse) | MPa | ≥45a | ≥47a |
| Low temperature tensile strength(transverse) | MPa | ≥80a | ≥81a |
| Water resistance tensile strength(transverse) | MPa | ≥35a | ≥35a |
| Aging resistance tensile strength(transverse) | MPa | ≥50a | ≥50a |
1. Sample water content less than 0.2% by weight.
2. Norm laboratory condition:(23±2)ºC and (50±10)% relative
humidity.
3. The specifications marked with "a" only applies to I-shape strip
otherwise, the specifications concluded between supplier and buyer
through consultation, shall be written in contract or purchase
order.
Packaging details:For all specifications/shapes, they could be packaged in linear, the length will be 6 meters, or customized.
For the Shape "I", "C", and some simple shapes, they can be packed
in rolls. 400-600 meters/roll.
Delivery details: shipped in 10-15 working days after payment
Before sales
1. introduce products in detail
2. recommend suitable solutions
3. provide with reference information
During manufacturing
1. provide with layout and engineering conditions
2. inform the processing status
3. offer related documents
After Sales
1. provide installation, commissioning and training
2. offer spare parts
3. Provide with necessary technical support