1. Pre-extruded profiles made from polyamide with 25 percent glass-fiber
2. Locked in place in ‘pockets’ extruded into two separate (inner and outer) aluminum extrusions
3. Enables finished assemblies with different finishes and colors on each surface
4. Aluminum extrusion pockets need to be ‘knurled’ prior to insertion of the polyamide profiles-and ‘rolled’ to create a structurally-secure finished assembly
5. The polyamide profiles can be supplied with ‘sealing-wire’ which give a reliable seal and enhanced shear strength when activated by heat e.g.-powder coating
6. The aluminum extrusions can be finished either before or after installation of the polyamide strips
Currently, there are two principal types of thermal barriers: polyamide thermal barrier strip and pour & debridge (P&D).
Our company only produce polyamide thermal barrier strip.
Polyamide is a plastic that insulates more than 500 times better than aluminum, so thermal break profiles have a much lower Uf value – and transmit much less heat or cold. As a result, a building stays warmer in winter while keeping the heat outside more easily in summer.
Why are thermal breaks important? Thermal breaks are essential for any external modern glazing system. Thermal bridging can be responsible for up to 30% of a property's heat loss. This lowers the homes energy efficiency, leading to higher heating bills.
Item | Unit | GB/T 23615.1-2009 | PW-Technical specification |
Density | g/cm3 | 1.3±0.05 | 1.28-1.35 |
Linear expansion coefficient | K-1 | (2.3-3.5)×10-5 | (2.3-3.5)×10-5 |
Vicat softening temperature | ºC | ≥230ºC | ≥233ºC |
Melting point | ºC | ≥240 | ≥240 |
Testing for tensile cracks | - | No cracks | No cracks |
Shore hardness | - | 80±5 | 80-85 |
Impact strength(Unnotched) | KJ/m2 | ≥35 | ≥38 |
Tensile strength(longitudinal) | MPa | ≥80a | ≥82a |
Elasticity modulus | MPa | ≥4500 | ≥4550 |
Elongation at break | % | ≥2.5 | ≥2.6 |
Tensile strength(transverse) | MPa | ≥70a | ≥70a |
High temperature tensile strength(transverse) | MPa | ≥45a | ≥47a |
Low temperature tensile strength(transverse) | MPa | ≥80a | ≥81a |
Water resistance tensile strength(transverse) | MPa |
| ≥35a |
Aging resistance tensile strength(transverse) | MPa | ≥50a | ≥50a |
1. Sample water content less than 0.2% by weight.
2. Norm laboratory condition:(23±2)ºC and (50±10)% relative
humidity.
3. The specifications marked with "a" only applies to I-shape strip
otherwise, the specifications concluded between supplier and buyer
through consultation, shall be written in contract or purchase
order.
Aluminium window has the disadvantage of limited thermal insulation. Its Uf value, which indicates the amount of heat that passes through a window profile, is simply too high. If your windows have standard aluminium profiles, your home may develop condensation, or even mould. Besides the resulting high repair costs, household mould also aggravates respiratory problems such as asthma.
But that disadvantage has now been completely eliminated if you install polyamide strips in aluminum windows. In fact, thanks to the development of a new invention known as thermal break profiles, aluminium is at least as good as its competitors. In these profiles, produced with specialized machines, a polyamide strip is placed between the inner and outer sections of the profile.
Polyamide is a plastic that insulates more than 500 times better than aluminium, so thermal break profiles have a much lower Uf value - and transmit much less heat or cold. As a result, your home stays warmer in winter, while keeping the heat outside more easily in summer.
Because PA66 is a hydrophilic substance, it will absorb the surrounding water. The rate and amount of water absorption depend on the ambient temperature, ambient humidity and storage period.
The relative humidity is higher in summer than in other short-term storage seasons. High moisture content (more than 2%) will affect the quality of wear-resistant strips.
When the insulation single bundle is removed from the shelf, it may be deformed. If it is not straightened in time, it will cause permanent deformation.
Therefore, it is recommended to keep it horizontal in a ventilated and dry environment, pay attention to waterproof, stay away from heat source, avoid stress and minimize bending.
If you have any specific questions, please contact us and we are happy to provide you with relevant services.