Rubber To Metal Bonding Agent 821 High Performance Cover-Coat
Adhesive
(Equivalent to Chemlok 252x/6253/6100/6016/6108,Cilbond 80ET,55E)
Rubber-to-metal bonding is used within the industry to isolate
vibration, reduce shock or to provide a seal for liquids, solids or
gases, in potentially demanding environments.
- Application
821 is a heat vulcanization bonding adhesive as cover coat for
rubber and various metals.
- Characteristics
- It is a high strength bonding adhesive for unvulcanized rubber and
metals coated with 813.The applicable rubbers include NR, CR, BR, SBR, PIPR, IIR, EPR,
EPDM.
- It is non-toxic, easily operated.
- It can be applied with different ways like dip coating, spraying,
brushing, and roller coating.
- It has excellent resistance to heating, water, solvent, oil, salt,
corrosion etc.
- It has high bonding strength, stability and long durability.
- Physical Properties
- Component: High polymer, organic compound, inorganic filler and
organic solvent.
- Color: Black
- Viscosity: (25℃, Brookfield LV2 30rpm) 200-350cps
- Solid Content: 23-27%
- Flash Point: 27℃
- Diluents: Xylene
- Solvent: Xylene
- Shelf life: 12 months in unopened containers (25℃)
- Applying 821
- Surface Preparation: All bonding surface must be contaminant (such as oil, rust, oxide
etc) free to reach optimum bonding effects. Surfaces should be
grit-blasted, and then ideally degreased. Apply 813 and wait it
becomes dry.
- Mixing: Homogeneous mix must be ensured before applying bonding agent.
- Dilution: Proper quantity dilutes can also be added according to dosage. The
diluted bonding agent cannot be stored for long time.
- Brushing: Unnecessary for dilution
- Roller coating: 100 portion of 821 with 10-15 portion diluents
- Dipping coating: 100 portion of 821 with 10-15 portion diluents
- Spraying: 100 portion of 821 with 50 portion diluents
- Coating thickness: The coating should be uniform. Drying coating thickness is 15-25
microns.
- Drying: After applying 821, it should be left for 45-60minutes to dry at
room temperature. Pre-warming or heating will speed up drying.
- Storage: It should be stored in dry environment at room temperature. Avoid
long time exposure in high humidity and temperature environment.
- After treatment: Before heating vulcanization, use cloth strip soaked with xylene
to clean the excessive bonding agent. Once cured, dilutes cannot
clean the bonding agent.
- Vulcanization: For optimum adhesion effects, rubber and bonding agent should be
vulcanized at the same time. When the coated parts are placed in
the mould, fill rubber inside and then close the mould to start
vulcanization immediately. Recommended vulcanization temperature is
145-185℃. Recommended vulcanization time is 5-60minutes.
Vulcanization pressure is according to practical situation.
- Notes
- Close the diluents container tightly after use.
- The diluents vapor is hazardous. Prevent long time inhalation or
skin contact in working place.
- Packing
3.5kg/drum; 18kg/drum