Qingdao Exceed Fine Chemicals Co.,Ltd |
Verified Suppliers
|
|
Rubber to Metal Bonding Adhesive 829GB
Equivalent to Chemlok 6411, Chemosil NL 411, Cilbond 80E, Megum
538/128
Application
Rubber to Metal Bonding Adhesive 829GB is mainly used as double
coating and post curing. It can help and promote various elastomers
to attach to the base rubber or various substrates. This product is
a mixture of polymer, organic compound and mineral filler dissolved
or dispersed in organic solvent system. Rubber to Metal Bonding
Adhesive 829GB has excellent resistance to harsh environment and
excellent spraying process. It can be sprayed with stock solution
by using appropriate process.
Used as a surface coating in conjunction with Dual Coat substrate
surface treatment agent, suitable for the following rubbers:
Natural rubber (NR), Natural butadiene rubber (NR+BR), Polyisoprene
rubber (IR), Butadiene rubber (BR), Chloroprene rubber (CR),
Styrene butadiene rubber (SBR), Nitrile butadiene rubber(NBR),
Butyl rubber (IIR), EPDM, etc
Characteristics
1. It is environmentally friendly, free of heavy metals, in line
with GB33372-2020, ROSH 2.0.
2. It has good settlement resistance.
3. It is suitable for vulcanized rubber
4. It has low viscosity, is suitable for industrial spraying.
5. It has good pre-drying resistance;
6. It has good weather resistance - heat resistance, water
resistance, solvent resistance, oil resistance, salt resistance,
corrosion resistance;
Physical Properties
1. Component: Polymers, organic compounds, inorganic fillers and
organic solvents
2. Color: Black
3. Viscosity: 150 ~ 600cps @25℃ , Brookfield LV2 30rpm
25 ~
50s @25℃ , No.3 Zahn Viscosity Cup 2
4. Flash Point: 25℃
5. Dilute release agent: Benzene containing solvents such as
xylene and toluene
6. Solubilizer: Xylene, dimethyl carbonate
7. Storage, Room temperature: Unopened container for 9 months
Applying Rubber to Metal Bonding Adhesive 829GB
1. Stirring: Rubber to Metal Bonding Adhesive 829GB in the
long-term storage process will have some precipitation at the
bottom of the container, before the glue must be fully stirred, to
achieve uniform mixing before use; If the gluing process is long,
stir at a high speed for 3-5 minutes at an interval of 2 hours.
2. Dilute: According to the actual operation needs, this product
can also add diluent for appropriate dilution. It is
recommended to dilute the diluted product according to the amount
used. The diluted product cannot be stored for a long time.
3. Brush coating method: no dilution is required;
4. Roller coating method: no dilution is required;
5. Dip: 100 parts of Rubber to Metal Bonding Adhesive 829GB plus
about 10-30 parts of diluent;
6. Spray method: 100 parts Rubber to Metal Bonding Adhesive 829GB
plus about 20-40 parts diluent.
7. Coating: This product can be applied by brush coating, dip
coating, roll coating, spray coating and other methods. Coating
should be uniform to avoid excessive spillover.
Cover coating: Dry film thickness DFT 12-25 μm. 20 μm is
recommended 20-40 μm for harsh environment;
Single coating: DFT 15- 25 μm,22 μm is recommended. For
PV-bonding above 25 μm;
8. Drying: Drying at room temperature takes about 45-60 minutes,
forced drying can shorten the drying time, recommended drying
temperature is 60-80 ℃.
9. Product storage: This product should be stored in dry and normal
temperature environment, avoid long-term exposure to high humidity
and high temperature environment.
10. Cleaning: Before heating vulcanization, dip a rag in xylene
solvent to remove excess treatment agent spilt around. Once cured,
solvent cannot be removed.
11. Vulcanization: Vulcanization of rubber and adhesive at the same
time can obtain the best bonding properties. When the coating is
placed in the molding mold, it should be quickly filled with rubber
vulcanization. The actual curing condition depends on the curing
condition of the rubber.
Notes
1. This product is volatile, please close the container after use.
2. Solvent steam is harmful, pay attention to fire prevention
in the workplace, pay attention to low ventilation, prevent
long-term inhalation or long-term skin contact.
3. Please refer to SDS for more safety information.