Yuhong Group Co.,Ltd |
Verified Suppliers
|
|
Yuhong Special Steel has been engaged in austenitic stainless steel, nickel alloy steel (Hastelloy, Monel, Inconel, Inconel) seamless welded pipes and pipes for more than 25 years, with annual sales of more than 80,000 tons of steel pipes and pipes. pipeline. Our customers are located in more than 45 countries including USA, Canada, UK, Germany, Italy, Chile, Colombia, Saudi Arabia, South Korea, Singapore, Australia, Poland and France.
Stainless steel coils are ideal for use in potentially corrosive environments, as well as for conveying liquids and gases for cooling, heating and other uses. From gas manifolds and piping to solar and medical equipment, YUHONG's stainless steel coils are effective in a wide range of applications.
Standard Specification:
ASTM A269/A269M: Standard Specification for General Seamless and
Welded Austenitic Stainless Steel Pipe
ASTM A312 / A312M-12: Standard Specification for Seamless, Welded,
and Re-cold Worked Austenitic Stainless Steel Pipe
ASTM A511 / A511M-12: Standard Specification for Seamless Stainless
Steel Mechanical Pipe
ASTM A789/A789M-10a: Standard Specification for General Seamless
and Welded Ferritic/Austenitic Stainless Steel Pipe
ASTM A790/A790M-11: Standard Specification for Seamless and Welded
Ferritic/Austenitic Stainless Steel Pipe
DIN 17456-2010: Universal seamless round stainless steel pipe.
DIN 17458-2010: Seamless round austenitic stainless steel tube
EN10216-5 CT 1/2: Stainless steel seamless pipes and tubes
GOST 9941-81: Seamless cold-worked and warm-worked tubes made of
corrosion-resistant steel.
Other standards such as BS and JIS can be supplied
ASTM | A312, A376, A358, A269, A249, A403, A182, A351 |
ASME | SA312, SA376, SA358, SA269, SA249,SA403, SA182, SA351 |
Material Grade:
American Standard | Austenitic Steel: TP304, TP304L, TP304H, TP304N, TP310S, TP316, TP316L, TP316Ti, TP316H, TP317, TP317L, TP321, TP321H, TP347, TP347H, 904L… Duplex Steel : S31803, S32101, S32205, S32304, S32750, S32760 Others: TP405, TP409, TP410, TP430, TP439,... |
Europen Standard | 1.4162, 1.4301, 1.4307,1.4362, 1.4401, 1.4404, 1.4410, 1.4438, 1.4462, 1.4501, 1.4539, 1.4541, 1.4550, 1.4571, 1.4841, 1.4845,1.4878, 1.4948, |
GOST | 08Х17Т, 08Х13, 12Х13, 12Х17, 15Х25Т, 04Х18Н10, 08Х20Н14С2, 08Х18Н12Б, 10Х17Н13М2Т, 10Х23Н18, 08Х18Н10, 08Х18Н10Т, 08Х18Н12Т, 08Х17Н15М3Т, 12Х18Н10Т, 12Х18Н12Т, 12Х18Н9, 17Х18Н9, 08Х22Н6Т, 06ХН28МДТ |
Size Range:
Production | Outside Diameter | Wall Thickness |
Seamless Pipe | 6.00mm-830mm | 0.5mm-48mm |
Specifications: ASTM A/ASME SA213/A249/A269/A312/A358 Pipes and Tubes Sizes (Seamless): 1/2" NB - 16" NB
Pipes and Tubes Sizes (ERW): 1/2" NB - 24" NB
Pipes and Tubes Sizes (EFW): 6" NB - 100" NB
Pipes and Tubes Wall Thickness available: Schedule 5S - Schedule XXS (heavier on request)
Pipe and Tubes Other Materials Testing: NACE MR0175, H2 SERVICE, OXYGEN SERVICE, CRYO SERVICE, etc.
Dimensions: All Pipe is manufactured and inspected/tested to the relevant standards including ASTM, ASME and API etc.
C | Cr | Mn | Mo | Ni | P | S | Si |
Max | Max | Max | Max | Max | |||
0.035% | 16% - 20% | 2.0% | 2% - 3% | 10% - 15% | 0.040% | 0.030% | 0.75% |
A269 TP304 Stainless Steel Seamless Tube Mechanical Properties
Density | 8.0 g/cm3 |
Melting Point | 1400 °C (2550 °F) |
Tensile Strength | Psi – 70000 , MPa – 515 |
Yield Strength (0.2%Offset) | Psi – 25000 , MPa – 205 |
Elongation | 35% |
316 is more resistant to atmospheric and other mild environments
than 304. It is resistant to dilute sulfuric acid solutions (i.e.
1-5%) up to 120°F. But in some oxidizing acids, 316 is not as
resistant as 304. 316 is susceptible to carbide precipitation when
exposed to temperatures in the 800° - 1500°F temperature range, and
therefore susceptible to intergranular corrosion in the as-welded
condition. Post-weld annealing will restore corrosion resistance.
316L has the same composition as 316 except that the carbon content
is kept below 0.03%. As expected, its general corrosion resistance
and other properties are very similar to Type 316. However, it does
provide resistance to intergranular corrosion in the as-welded
condition or when exposed for short periods of time in the
temperature range of 800° - 1500°F. When carbide precipitation
ranges are unavoidable and post-weld annealing is not feasible,
316L is recommended. However, prolonged exposure in this range may
make the material brittle and make it susceptible to intergranular
attack. The maximum temperature for scaling resistance is
approximately 1650°F in continuous use and 1500°F in intermittent
use.
May be susceptible to chloride stress corrosion cracking.
Non-hardenable; non-magnetic in the annealed state, slightly
magnetic when cold-worked. Improves corrosion resistance to
chlorides.