ASTM B 163 ASTM B 407 Nickel Alloy incoloy 825 Tubo sem costura Nickel Alloy Pipe 100% ET E HT

ASTM B 163 ASTM B 407 Nickel Alloy incoloy 825 Tubo sem costura Nickel Alloy Pipe 100% ET E HT

Incoloy Alloy 825

Common Trade Names: Incoloy 825, Alloy 825, Nickelvac 825, Nicrofer 4241.

INCOLOY alloy 825 (UNS N08825, W.Nr. 2.4858) is a nickel-iron-chromium alloy with additions of molybdenum, copper, and titanium. The nickel content is sufficient for

resistance to chloride-ion stress-corrosion cracking. The nickel, in conjunction with the molybdenum and

copper, also gives outstanding resistance to reducing environments such as those containing sulfuric and

phosphoric acids. The molybdenum also aids resistance to pitting and crevice corrosion. The alloy’s

chromium content confers resistance to a variety of oxidizing substances such as nitric acid, nitrates and

oxidizing salt. The titanium addition serves, with an appropriate heat treatment, to stabilize the alloy against

sensitization to intergranular corrosion.

Specifications

INCOLOY Alloy 825 is designated as UNS N08825 and Werkstoff Number 2.4858. It is listed in NACE

MR0175 for oil and gas service.

Rod, Bar, Wire and Forging Stock: BS 3076NA16, ASTM B 425, ASTM B 564, ASME SB 425, ASME

SB 564, ASME Code Case N-572, DIN 17752, DIN 17753, DIN 17754, VdTÜV 432, ISO 9723, ISO 9724,

ISO 9725.

Plate, Sheet and Strip: BS 3072NA16, BS 3073NA16, ASTM B 424, ASTM B 906, ASME SB 424, ASME

SB 906, DIN 17750, VdTÜV 432, ISO 6208.

Pipe and Tube: BS 3074NA16, ASTM B 163, ASTM B 423, ASTM B 704, ASTM B 705, ASTM B 751,

ASTM B 775, ASTM B 829, ASME SB 163, ASME SB 423, ASME SB 704, ASME SB 705, ASME SB 751,

ASME SB 775, ASME SB 829, ASME Code Case 1936, DIN 17751, VdTÜV 432, ISO 6207.
Others: ASTM B 366, ASME SB 366, DIN 17744

Chemical Composition

Nickel..........................................................................38.0-46.0
Iron...............................................................................22.0min.
Chromium....................................................................19.5-23.5
Molybdenum ...................................................................2.5-3.5
Copper............................................................................1.5-3.0
Titanium...........................................................................0.6-1.2
Carbon........................................................................0.05 max.
Manganese...................................................................1.0max.
Sulfur..........................................................................0.03max.
Silicon...........................................................................0.5max.
Aluminum......................................................................0.2 max.

INCOLOY 825 SEAMLESS TUBES UNS No: UNS N08825 Werkstoff Nr: 2.4858 The above names are trade names and/or trademarks of specific manufactures including Special Metal Corporation. Prosaic Steel & Alloy is not affiliated with any manufacturer(s). Orders will be filled to meet specifications from any available source(s). Names are listed solely for reference to help identify products consistent with listed specificationsto help identify products consistent with listed specifications. Specifications Incoloy 825 Tubes- UNS N08825 Product Range -Seamless tubes 6 mm OD x 0.7 mm to 50.8 mm OD x 3 mm thk. Specifications - B 163 / B 423. Finish Conditions- Cold Drawn Solution Annealed & Pickled / Cold Drawn Bright annealed / NACE MRO 175

Incoloy alloy 825 is a nickel-iron-chromium alloy with additions of copper, molybdenum and titanium. The alloy's chemical composition is designed to provide exceptional resistance to many corrosive environments. The nickel content is sufficient for resistance to chloride-ion stress corrosion cracking. The nickel, in conjunction with the molybdenum and copper, also gives outstanding resistance to reducing environments such as those containing sulfuric and phosphoric acids. The molybdenum also aids resistance to pitting and crevice corrosion. The alloy's chromium content confers resistance to a variety of oxidizing substances such as nitrates, nitric acid and oxidizing salts. The titanium addition serves, with an appropriate heat treatment, to stabilize the alloy against sensitization to intergranular corrosion. The resistance of Incoloy 825 to general and localized corrosion under diverse conditions gives the alloy broad usefulness. Applications include chemical processing, pollution control, oil and gas recovery, acid production, pickling operations, nuclear fuel reprocessing and handling of radioactive wastes.
.The outstanding property of Incoloy 825 is its corrosion resistance. In reducing & oxidising conditions, Incoloy 825 resists general corrosion, pitting & crevice corrosion, intergranular corrosion and stress corrosion cracking. It is particularly useful in sulphuric & phosphoric acids, sulphur containing flue gases, sour gas and oil wells and sea water.
Incoloy 825 is approved for pressure vessel operating temperatures up to 525C (AS1210, AS4041), 538C (ASME Boiler & Pressure Vessel Code, Sections I, III, VIII, IX, Cases 1936, N-188). Brittle phases may form in alloy 825 at temperatures above ~ 540C, so it is not normally used at these temperatures, where creep-rupture properties would be design factors.
Chemical Composition of Incoloy Alloy 825
Table 1. Chemical composition of Incoloy Alloy 825 (ASTM B163 Heat exchanger tube)

Tensile Properties of Incoloy Alloy 825
Table 2. Typical room temperature tensile properties (not for design. Consult the relevant material or product specification for design values)

Corrosion Resistance
The outstanding property of Incoloy 825 is its corrosion resistance. In reducing & oxidising conditions, Incoloy 825 resists general corrosion, pitting & crevice corrosion, intergranular corrosion and stress corrosion cracking. It is particularly useful in sulphuric & phosphoric acids, sulphur containing flue gases, sour gas and oil wells and sea water.

Incoloy 825 can be readily hot or cold worked. Hot working should be in the range 870 1180C, finishing at 870 980C. For maximum corrosion resistance hot worked parts should be stabilise annealed before use. The alloy is easier to cold form than stainless steels.
Heat Treatment
Incoloy 825 is stabilise annealed at 940C. The softest structure is obtained at 980C. Sections heavier than sheet, strip and wire should be quenched to avoid sensitisation.
Application
Incoloy 825 is the material of choice in a wide variety of applications up to a temperature of approximately 550C (1020F),

• Chemical Processing
• Nuclear Fuel Reprocessing
• Acid Production
• Pickling Equipment
•