Inconel 601 is a nickel-chromium alloy used for applications that require resistance to corrosion and heat. This nickel alloy stands out due to its resistance to high temperature oxidation, remaining highly resistant to oxidation through 2200° F. Alloy 601 develops a tightly adherent oxide scale which resists spalling even under conditions of severe thermal cycling. This nickel alloy has good high temperature strength, and retains its ductility after long service exposure. It has good resistance to aqueous corrosion, high mechanical strength, and is readily formed, machined and welded. Inconel 601's properties make it a material of broad utility in fields like thermal processing, chemical processing, pollution control, aerospace, and power generation. However, alloy 601 is not suggested for use in strongly reducing, sulfur bearing environments.
Specification
ASTM B167-18 Standard Specification for Nickel-Chromium-Aluminum Alloys (UNS N06699), Nickel-Chromium-Iron Alloys (UNS NO6600, NO6601, NO6603, NO6690, NO6693, NO6025, NO6045, and NO6696), Nickel-Chromium-Cobalt-Molybdenum Alloy (UNS NO6617), Nickel-Iron-Chromium-Tungsten Alloy (UNS NO6674), and Nickel-Chromium-Molybdenum-Copper Alloy (UNS NO6235) Seamless Pipe and Tube.
Specifications | ASTM B167, B517 / ASME SB167, SB517 |
Standard | ASTM, ASME and API |
Pipe Size | Range 15"NB – 150"NB |
Outside Diameter | 6.35 mm OD upto 254 mm OD in 0.6 TO 20 mm thickness. |
Length | Single Random, Double Random & Required Length |
Thickness | 0.3mm – 50 mm |
Schedule | SCH20, SCH30, SCH40, STD, SCH80, XS, SCH60, SCH120, SCH140, SCH160, XXS |
Type | Seamless, Welded, ERW |
End | Plain End, Beveled End, Treaded |
Equivalent Grades for Inconel 601 Pipe
Grade |
UNS No | Old British | Euronorm | GOST | Japanese JIS | ||
BS | En | No | AFNOR | ||||
Inconel 601 | N06601 | NA 49 | NiCr23Fe | 2.4851 | NC23FeA | XH60BT | NCF 601 |
Chemical Composition
Grade | C | Mn | Si | Fe | S | Cr | Cu | Ni | |
Inconel 601 | min. | – | – | – | Bal | – | 21.0 | – | 58.0 |
max. | 0.10 | 1.0 | 0.5 | Bal | 0.015 | 25.0 | 1.0 | 63.0 | |
Mechanical Properties
Grade |
Tensile Strength (MPa) min |
Yield Strength 0.2% Proof (MPa) min |
Elongation (% in 50mm) min | Hardness | |
Rockwell B (HR B) max | Brinell (HB) max | ||||
Inconel 601 | Psi – 95,000 , MPa -655 | Psi – 45,000 , MPa – 310 | 40 | – | – |
Applications
1. Chemical Processing.
2. Aerospace.
3. Heat treating industry.
4. Power generation.
5. Heat treating muffles and retorts.
6. Radiant tubes.
7. Catalyst support grids in nitric acid production.
8. Steam superheater tube supports.