Wuxi Wilke Metal Materials Co., Ltd. |
Verified Suppliers
|
|
1. chemical composition%:
C:≤0.15,Carbon C: ≤0.030
Silicon Si: ≤1.00
Manganese Mn: ≤2.00
Sulfur S: ≤0.030
Phosphorus P: ≤0.045
Chromium Cr: 16.00~18.00
Nickel Ni: 10.00~14.00
Molybdenum Mo: 2.00~3.00
2. Mechanical properties:
Tensile strength σb (MPa): ≥480
Conditional yield strength σ0.2 (MPa): ≥177
Elongation δ5 (%): ≥40
Area shrinkage ψ (%): ≥60
Hardness: ≤187HB; ≤90HRB; ≤200HV
Density: 7.98g/cm3;
Specific heat capacity ratio (20℃): 0.502J/(g*K).
Q:What is stainless steel usually used for?
A:Stainless steel is popularly used for cookware, kitchen utensils and cutlery. This is because it's hardwearing, corrosion resistant, and it doesn't affect the flavour of the food when used for food storage or production. Due to the resistance level, foods with high acidity won't cause damage.
Standard | ASTM, GB, JIS, AISI, EN, DIN |
Material | 201, 304, 304L, 304N, 304LN, 305, 309S,316, 316L, 316Ti, 317, 321, 405, 430, 904L, 2205, etc |
Surface | NO.1, NO.4, 2B, BA, Hair Link, 8K, Brush, Embossed and Mirror Finished or as your required |
Width | 10mm-600mm |
Length | customized |
Thickness | 0.3mm-3mm(cold rolled) 3mm-16mm(hot rolled) |
Application | Petroleum and chemical industries, furniture, kitchen appliances, decoration, Construction field, equipment and medical devices |
Package | Standard export sea-worthy packing: 1. Bundle package 2. Container or bulk 3. Wooden case, wooden pallet package 4. Special according to customer’s request |
Surface | Characteristic | Processing Technology |
N0.1 | Original | Pickled after hot rolling |
2D | Blunt | Hot rolling + annealing shot peening pickling + cold rolling + annealing pickling |
2B | Blurred | Hot rolling + annealing shot peening pickling + cold rolling + annealing pickling + tempering rolling |
N0.3 | Matte | Polishing and tempering rolling with 100-120 mesh abrasive materials |
N0.4 | Matte | Polishing and tempering rolling with 150-180 mesh abrasive material |
HL | Brushed | Grind the surface of the steel belt with an appropriate grinding grain size to make it show a certain longitudinal texture |
BA | Bright | The surface is annealed and shows high reflectivity |
6K | Mirror | Rough grinding and polishing |
8K | Mirror | Fine grinding and polishing |