1060 H112 6.35*0.8mm Aluminium Tube Coil for Air Conditioner/Aluminum Pipe for HVAC Use
Aluminum tubes are especially suited to long production runs for industrial applications. Mainly be used on the air-conditioner, freezer, refrigeration, Condenser, intercooler, evaporator, warm wind movement, air conditioner pipeline, car radiator, etc.
General size:
1) Grade: 1050 1060 1070 1100 3003 3102 3103 etc
2) Outside Diameter: 4mm-22.22mm
3) Wall Thickness: 0.4mm-2.0mm
4) Length: Not fixed, around 40-85kg/reel depend on the size of the
tube
5) Coil size:
Coil I.D: 400mm/500mm,coil O. D: 750mm-1200mm , coil high:
310mm/400mm
6) Aluminum tube Temper: O H112 H14 H18 H24 H28 etc
Production Standard: ASTM B241 ASTM B241M GB etc.
Size(inch) | O.D(mm) | W.T(mm) | Meters per coil |
1/4" | 6.35 | 0.8 | 15 20 30 50 |
5/16" | 7.94 | 0.8 | 15 20 30 50 |
3/8" | 9.52 | 0.8 | 15 20 30 50 |
1/2" | 12.7 | 0.8 | 15 20 30 50 |
5/8" | 15.88 | 1 | 15 20 30 50 |
3/4" | 19.05 | 1 | 15 20 30 50 |
| A1050 Aluminium Chemical Composition | |||||||||
| Al | Si | Cu | Mg | Zn | Mn | Ti | V | Fe | Others |
| 99.5~100 | 0~0.25 | 0~0.05 | 0~0.05 | 0~0.05 | 0~0.05 | 0~0.03 | 0~0.05 | 0~0.40 | 0~0.03 |
| A1060 Aluminium Chemical Composition | |||||||||
| Al | Si | Cu | Mg | Zn | Mn | Ti | V | Fe | Others |
| 99.6-100 | 0~0.25 | 0~0.05 | 0~0.03 | 0~0.05 | 0~0.03 | 0~0.03 | / | 0~0.35 | |
| A1070 Aluminium Chemical Composition | |||||||||
| Al | Si | Cu | Mg | Zn | Mn | Ti | V | Fe | Others |
| 99.7~100 | 0~0.2 | 0~0.04 | 0~0.03 | 0~0.04 | 0~0.03 | 0~0.03 | 0~0.05 | 0~0.25 | |
| Physical Property of 1050 1060 1070 aluminum tube pipe | ||||||
| Alloy | Temper | Wall thickness /mm | Room temperature Test Result | |||
| Tension Strength/MPa | Yield Strength/MPa | Elongation/% | ||||
| A50mm | A | |||||
| Not less than | ||||||
| 1050 | O, H111 | All | 60 ~ 100 | 20 | 25 | 23 |
| H112 | All | 60 | 20 | 25 | 23 | |
| F | All | － | － | － | － | |
| 1060 | O | All | 60 ~ 95 | 15 | 25 | 22 |
| H112 | All | 60 | － | 25 | 22 | |
| 1070 | O | All | 60 ~ 95 | － | 25 | 22 |
| H112 | All | 60 | 20 | 25 | 22 | |