Precision tubes for hydraulic systems, automobiles, machinery, and other precision steel pipe, finish, cleanliness, there are areas of high mechanical performance requirements.
Chemical Composition(%) & Mechanical Properties:
Chemical Composition(%): | ||||||
Standard | Steel Grade | C | Si | Mn | P | S |
JIS G3445 | STKM11A | ≤0.12 | ≤0.35 | ≤0.60 | ≤0.040 | ≤0.040 |
Mechanical Properties: | ||||
Standard | Steel Grade | Yield Strength min.(Mpa) | Tensile Strength min.(Mpa) | Elongation A min.(%) |
JIS G3445 | STKM11A | / | 290 | 35 |
Pipe Tolerance Table | ||||
Name | Rang(mm) | German Standard(mm) | Corporate Internal Control Standards(mm) | Special High-Precision(mm) |
Outer Diameter | 4-30 | ±0.08 | ±0.05 | ±0.03 |
| 31-40 | ±0.15 | ±0.05 | ±0.03 |
| 41-50 | ±0.20 | ±0.08 | ±0.03 |
| 51-60 | ±0.25 | ±0.08 | ±0.03 |
Wall thickness | 0.5-7 | ±10% | ±10%,Min±0.05 | ±10%,Min±0.03 |
Length | +/-10mm | Automotive industry pipe length can be cut according to customer requirements. | ||
Heat treatment process delivery conditions: | |
Delivery Condition | Heat Treatment Process |
+C | Cold drawn / hard. After the final cold forming no heat treatment. |
+LC | Cold drawn/soft. After the final heat treatment-limiting deformation, cold drawn, allowing a degree of cold deformation |
+SR | Steel heat treatment is applied after the last cold deformation process, the result of state steel after due process, the residual stress deformation and machining makes a certain degree of difficulty increases. |
+A | In the final step of the steel pipe after cold deformation, placed in a controlled atmosphere furnace for annealing. |
+N | In the final step of the steel pipe after cold deformation, placed in a controlled atmosphere furnace at a temperature above the phase transition point to continue annealing. |