EN 10288 Stainless Steel Plate Ring Circle 1.4541 80.0mm Heat Resistant

Country/Region china
City & Province wuxi jiangsu
Categories Other Metals & Metal Products
InquireNow

Product Details

EN 10288 1.4541 Heat Resistant Stainless Steel Plate / Stainless Steel Ring / Stainless Steel Circle
 
Detail information of the stainless steel plate:

 

Commodity

321 stainless steel plate

Grade

201,202,304,304L,316,316L,310S,309S,321,301,310,410,420,430,904L 2205 2507 

Brand

TISCO ,BAOSTEEL,POSCO,JISCO,LISCO

Certification

SGS, BV, IQI, TUV, ISO, etc

Thickness

3.0 - 80.0mm

Width

1000,1219,1250,1500mm, or as your requirements

Length

2000,2438,2500,3000,6000mm, or as your requirements

Surface

No.1, 2B, BA, 8K Mirror, Hairline, Satin, Embossed, Brush, No.4, HL, Matt, PVC film, Laser film

Standard

ASTM,AISI,SUS,JIS,EN,DIN,GB, ASME, etc

Delivery time

5-7 days after confirming the order

MOQ

1 Ton

Advantages

Showing the splendor of your quality, wearresistant as well.
Strong corrosion resistance and decorative effect, durable and beautiful in good taste.

 

Grades 321 and 347 are the basic austenitic 18/8 steel (Grade 304) stabilized by Titanium (321) or Niobium (347) additions. These grades are used because they are not sensitive to intergranular corrosion after heating within the carbide precipitation range of 425-850 °C. Grade 321 is the grade of choice for applications in the temperature range of up to about 900 °C, combining high strength, resistance to scaling and phase stability with resistance to subsequent aqueous corrosion.

Grade 321H is a modification of 321 with higher carbon content, to provide improved high-temperature strength.

A limitation with 321 is that titanium does not transfer well across a high-temperature arc, so it is not recommended as a welding consumable. In this case grade 347 is preferred - the niobium performs the same carbide stabilization task but can be transferred across a welding arc. Grade 347 is, therefore, the standard consumable for welding 321. Grade 347 is only occasionally used as parent plate material.

Like other austenitic grades, 321 and 347 have excellent forming and welding characteristics, are readily brake or roll-formed and have outstanding welding characteristics. Post-weld annealing is not required. They also have excellent toughness, even down to cryogenic temperatures. Grade 321 does not polish well, so is not recommended for decorative applications.

Grade 304L is more readily available in most product forms, and so is generally used in preference to 321 if the requirement is simply for resistance to intergranular corrosion after welding. However, 304L has lower hot strength than 321 and so is not the best choice if the requirement is resistance to an operating environment over about 500 °C.

These properties are specified for the flat-rolled products (plate, sheet, and coil) in ASTM A240/A240M. Similar but not necessarily identical properties are specified for other products such as pipe and bar in their respective specifications.

Composition of 321 stainless steel plate

Typical compositional ranges for grade 321 stainless sheets of steel are given in table 1.

Table 1. Composition ranges for 321-grade stainless steel

Grade

 

C

Mn

Si

P

S

Cr

Mo

Ni

N

Other

321

min.
max

-
0.08

2.00

0.75

0.045

0.030

17.0
19.0

-

9.0
12.0

0.10

Ti=5(C+N)
0.70

321H

min.
max

0.04
0.10

2.00

0.75

0.045

0.030

17.0
19.0

-

9.0
12.0

-

Ti=4(C+N)
0.70

347

min.
max

0.08

2.00

0.75

0.045

0.030

17.0
19.0

-

9.0
13.0

-

Nb=10(C+N)
1.0

 

Mechanical Properties 321 stainless steel plate

Typical mechanical properties for grade 321 stainless sheets of steel are given in table 2.

Table 2. Mechanical properties of 321-grade stainless steel

Grade

Tensile Strength (MPa) min

Yield Strength 0.2% Proof (MPa) min

Elongation (% in 50 mm) min

Hardness

Rockwell B (HR B) max

Brinell (HB) max

321

515

205

40

95

217

321H

515

205

40

95

217

347

515

205

40

92

201

 

 

Typical applications include:

  • Aircraft exhaust manifolds

  • Expansion joints

  • Bellows

  • Furnace parts

  • Heating element tubing

  • Heat Exchangers

  • Woven or welded screens for high-temperature mineral processing

  • Spiral Welded tube for burner pipes and flues

 

Products show:

Hot Products

SS 904L Plate Specifications 2B PE, No. 4 PE, BA PE, 2B Finish 904l stainless steel sheet and 904L ...
316LVM / 1.4441 Implant steel with improved corrosion resistance compared to AISI 316L. Application ...
Nickel Alloy Incoloy 825 Sheet ASTM B424 Din 2.4858 Cold Rolled Alloy Steel Sheet Incoloy 825 Sheet ...
Product Details Description Type 440A is a corrosion resistant martensitic stainless steel ...
444 Stainless steel sheet manufacturer SUS444 (00Cr18Mo2) is a ferritic stainless steel with ultra...
Technical Data Sheet Alloy 75 (UNS N06075, Nimonic 75) is a 80/20 nickel-chromium alloy with ...