304 stainless steel square bar is an excellent candidate for most processing techniques as well as both indoor and outdoor applications. This product, designed for close tolerances, has a semi-smooth, dull grey finish and sharp defined edges with accurate dimensions throughout length. 304 stainless steel is a high strength material with excellent corrosion resistance making it ideal for structural support, shafts, jigs, key stock, sculptures, and other architectural uses. ASTM A276-10 is the standard specification for stainless steel bars and shapes.
Grade | 201,202,304,316L,310S 2205 etc. | |||
Standard | JIS, AISI, ASTM, DIN, TUV,BV,SUS,etc | |||
Thickness | 4 - 500mm | |||
Width range | Customized | |||
Length | Customized | |||
Size | 6m, 12m, as Requirement | |||
Finish | 2B, BA, No.4, 8k, Brushed,Hairline,PVD Coating,Sandblasted | |||
Color | Golden, Black , Sapphire Blue, Brown, Rose gold, Bronze, Purple,
gray, silver, Champagne, violet, blue diamond, etc | |||
Export to | Korea,Turkey,Kuwait,Malaysia,Vietnam,India,Jordan,etc | |||
Application | Interior/exterior/architectural/bathroom decoration, elevator
decoration, hotel decoration, kitchen equipment, ceiling, cabinet, | |||
Lead time | 7 to 25 working days after the receipt of 30% deposit | |||
Payment terms | 30%TT for deposit, 70% balance before shipment or LC at sight | |||
Packing | Wooden pallet or according to customer's request | |||
| Chemical Composition Reference | |||||||
| Grade | C≤ | Si≤ | Mn≤ | P≤ | S≤ | Ni | Cr |
| 201 | 0.15 | 1.00 | 5.50-7.50 | 0.5 | 0.03 | 3.50-5.50 | 16.00-18.00 |
| 202 | 0.15 | 1.00 | 7.50-10.00 | 0.5 | 0.03 | 4.00-6.00 | 17.00-19.00 |
| 304 | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | 8.00-11.00 | 18.00-20.00 |
| 304L | 0.03 | 1.00 | 2.00 | 0.045 | 0.03 | 8.00-12.00 | 18.00-20.00 |
| 309 | 0.20 | 1.00 | 2.00 | 0.04 | 0.03 | 12.00-15.00 | 22.00-24.00 |
| 309S | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | 12.00-15.00 | 22.00-24.00 |
| 310 | 0.25 | 1.00 | 2.00 | 0.04 | 0.03 | 19.00-22.00 | 24.00-26.00 |
| 310S | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | 19.00-22.00 | 24.00-26.00 |
| 316 | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | 10.00-14.00 | 16.00-18.00 |
| 316L | 0.03 | 1.00 | 2.00 | 0.045 | 0.03 | 10.00-14.00 | 16.00-18.00 |
| 316Ti | 0.08 | 1.00 | 2.00 | 0.045 | 0.03 | 10.00-14.00 | 16.00-18.00 |
| 410 | 0.15 | 1.00 | 1.00 | 0.04 | 0.03 | 0.60 | 11.50-13.50 |
| 430 | 0.12 | 0.12 | 1.00 | 0.04 | 0.03 | 0.60 | 16.00-18.00 |
MECHANICAL INFORMATION | ||
| Imperial | Metric | |
| Density | 0.289 lb/in3 | 8.0 g/cc |
| Ultimate Tensile Strength | 73,200psi | 310 MPa |
| Yield Tensile Strength | 31,200psi | 276 MPa |
| Melting Point | 2,550 - 2,651°F | 1,400 - 1,455°C |
| Temper | Annealed |
| Hardness Rockwell | B70 |
| Hardness Brinell | 123 |