JIANGSU MITTEL STEEL INDUSTRIAL LIMITED |
Verified Suppliers
|
|
Min. % | Max % | ||||||||||
Carbon | 0.12 | 0.20 | |||||||||
Silicon | 0.00 | 1.00 | |||||||||
Manganese | 0.00 | 1.00 | |||||||||
Nickel | 1.25 | 3.00 | |||||||||
Chromium | 15.00 | 18.00 | |||||||||
Phosphorous | 0.00 | 0.04 | |||||||||
Sulphur | 0.00 | 0.03 |
DENSITY (G/CM 3) | 8.0 |
DENSITY (LB/IN 3) | 0.289 |
MELTING POINT (°C) | 1400 – 1455 |
MELTING POINT (°F) | 2550 – 2650 |
Tensile Strength : Unit – ksi (MPa) , Minimum
Yeild Strength : 0.2 % Offset , Unit – ksi (MPa) , Minimum
Elongation : in 2″, Unit : % , Minimum
Hardness : Rockwell , Maximum
Condition | Annealed
| *T | |||||||||
Tensile Strength Mpa | Min | 850 | |||||||||
Max | 1000 | ||||||||||
0.2% Yield Strength Mpa | Min | 635 | |||||||||
Elongation on 5.65√S0 % | Min | 11 | |||||||||
Izod Impact Valua J mm | Min | 63 34 63 20 | |||||||||
Hardness HB | Min | 248 | |||||||||
Max | 277 | 302 | |||||||||
*Material stocked generally in condition T. NB. Check the mill certificate if critical for end use. |