301 stainless steel sheet in different hardness type 2B BA finish width as client request
Description:
Grade 301 is a high work-hardening rate austenitic stainless steel.
It can be supplied with a tensile strength of up to over 1300 MPa
in strip and wire forms, to produce tempers in the range of 1/16
Hard to Full Hard. The controlled analysis of Grade 301 enables it
to retain sufficient ductility in conditions up to 1/2 Hard
conditions to be roll or brake formed into aircraft, architectural
and particularly rail car structural components. However, 3/4 to
Full Hard tempers should be used whenever high wear resistance and
spring features are required in components of simple form designs.
Grade 301L with low carbon is preferred for improved ductility or
if heavy sections are to be welded, and another variant 301LN has a
higher nitrogen content to compensate for the lower carbon.
ASTM A666 covers all three variants, and some are also included in
Japanese specification JIS G4305 and Euronorm EN 10088-2.
Composition Specification (%)
Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
301 | min. max. | - 0.15 | - 2.0 | - 1.0 | - 0.045 | - 0.030 | 16.0 18.0 | - | 6.0 8.0 | - 0.10 |
301L | min. max. | - 0.03 | - 2.0 | - 1.0 | - 0.045 | - 0.030 | 16.0 18.0 | - | 6.0 8.0 | - 0.20 |
301LN | min. max. | - 0.03 | - 2.0 | - 1.0 | - 0.045 | - 0.015 | 16.5 18.5 | - | 6.0 8.0 | 0.07 0.20 |
Mechanical Property Specification (Grade 301 – other values for 301L and 301LN)
Grade 301 Temper ASTM A666 | Tensile Strength (MPa)min. | Yield Strength 0.2% Proof (MPa)min. | Elongation (% in 50mm) (thick.>0.76mm)min. | Bend Test (1.27 - 4.76mm thick) | Hardness Rockwell C (Note 2) | |
Bend Angle (°) | Factor (Note 1) | |||||
Annealed | 515 | 205 | 40 | 180 | 1 | |
1/16 Hard | 620 | 310 | 40 | 180 | 1 | |
1/8 Hard | 690 | 380 | 40 | 180 | 1 | |
1/4 Hard | 860 | 515 | 25 | 90 | 2 | 25 – 32 |
1/2 Hard | 1035 | 760 | 18 | 90 | 2 | 32 – 37 |
3/4 Hard | 1205 | 930 | 12 | 90 | 3 | 37 – 41 |
Full Hard | 1275 | 965 | 9 | 90 | 5 | 41+ |
Notes 1. Bend test is around a diameter of the Bend Factor multiplied by the steel thickness. 2. Hardness values are typical industry standard – there are no specified limits. |
Physical Properties (Grades 301, 301L and 301LN - typical values in the annealed condition)
Grade | Density (kg/m3) | Elastic Modulus (GPa) | Mean Coefficient of Thermal Expansion | Thermal Conductivity | Specific Heat 0-100°C ( J/kg.K) | Electrical Resistivity (nW.m) | |||
0-100°C (mm/m/°C) | 0-315°C (mm/m/°C) | 0-538°C (mm/m/°C) | at 100°C (W/m.K) | at 500°C (W/m.K) | |||||
All | 7900 | 193 | 17.0 | 17.2 | 18.2 | 16.3 | 21.5 | 500 | 720 |
Grade Specification Comparison
Grade | European | Japanese JIS | |
No | Name | ||
301 | 1.4319 | X5CrNi17-7 | SUS 301 |
301L | - | - | SUS301L |
301LN | 1.4318 | X2CrNiN18-7 | - |
These comparisons are approximate only. The list is intended as a comparison of functionally similar materials not as a schedule of contractual equivalents. If exact equivalents are needed original specifications must be consulted. Different comparisons apply to grades 301L and 301LN. |
Corrosion Resistance
Corrosion resistance is similar to that of 304. Good resistance in
applications involving external exposure to mildly corrosive
conditions at ambient temperatures.
Heat Resistance
Good oxidation resistance in intermittent service to 840°C and in
continuous service to 900°C, although not usually chosen for this
environment. Exposure to temperatures above about 400°C will result
in progressive removal of work hardening effects; at approximately
800°C the strength will be similar to an annealed 301. In creep
applications a work hardened grade 301 can even reduce to lower
strength than an annealed 301.
Heat Treatment
Solution Treatment (Annealing) Heat to 1010-1120°C and cool
rapidly. Use low side of range for intermediate annealing. This
grade cannot be hardened by thermal treatment.
Cold WorkingGrade 301 and its low carbon variants are used where a
high strength stainless steel is
Grade Data Sheet
301 301L 301LN
The grades work harden at the very high rate of approximately
14MPa/%Ra (14MPa increase in tensile strength for each 1% reduction
of area of cold work), resulting in high achievable strengths from
cold rolling and from roll forming. The strain-hardened austenite
is at least partially transformed to martensite by this work.
Despite the high strengths achieved there is still enough residual
ductility to enable significant cold deformation. Although
non-magnetic in the annealed condition, when cold worked the grades
become strongly attracted to a magnet.
Welding
Good characteristics suited to all standard methods. Welds in Grade
301 must be annealed for maximum corrosion resistance; this is not
necessary in 301L or 301LN. Welding and post weld annealing will
both remove high strength induced by prior cold rolling.
Spot welding is commonly used to assemble cold rolled 301
components. The very small heat affected zone associated with this
rapid welding technique results in little reduction of overall
component strength.
Typical Applications
Rail car structural components - often roll formed, brake pressed
or stretch formed to profiles but also used flat. Airframe
sections. Highway trailer components. Automotive wheel covers,
wiper blade holders and clips. Toaster springs, stove element
clips. Screen frames, curtain walls.
Specified Properties
The properties for Grade 301 are specified for flat rolled product (plate, sheet and coil) in ASTM A666. Similar but not identical mechanical properties are specified in EN 10088.2 and JIS G4305 and in proprietary specifications.