High Harden NM500 / AR500 / Hardox 500 Steel Plate for Engineering Machinery
Products Specification of Wear Resistant Steel Plate
| Products Name | Abrasion Resistant Steel Plate |
| Thickness | 4.0 - 40.0mm |
| Width | 100 - 2200mm custom cutting any size as request |
| Length | 6m 8m 10m 11.5m 12m or cutting any length as request |
| Standard | ASTM JIS GB EN |
| MOQ | 500 Kgs |
| Deliver time | 7 - 14 days |
| Loading Port | Shanghai Port |
| Packing | wooden pallets |
| Other Grade | AR400 / AR450 / AR500 / AR600 NM400 NM450 NM500 NM600 |
| Service | Cutting, Heat treatment |
GB/T24186 NM500 abrasion resistant steel plate is an abrasion
resistant plate with a hardness of 500 HBW. intended for
applications where demands are mposed on abrasion resistance in
combination with good cold bending properties. GB/T24186 NM500
abrasion resistant steel plate offers very goodweldability.
GB/T24186 NM500 abrasion resistant steel plate is a high-strength
wear-resisting steel plate, which has a high abrasion resistance.
Brinell hardness value up to 500(HBW) is mainly used to provide
protection for wear-resisting occasions or parts, so as to prolong
the service life of the equipment, reduce the maintenance and stop
caused by maintenance, and correspondingly reduce the investment of
funds.
| Specifications | GB/T24186 NM500 abrasion resistant steel plate |
| Standard | GB/T24186 |
| Specialize | Shim Sheet, Perforated Sheet, B. Q. Profile. |
| Length | 50mm-18000mm |
| Width | 50mm-4020mm |
| Thickness | 1.2mm-300mm |
| Hardness | Soft, Hard, Half Hard, Quarter Hard, Spring Hard etc. |
Profiled: According to drawing.
Inspection: Chemical analysis, Metallographic, Mechnical analysis, Ultrasonic testing, Impact testing, Hardness testing, Surface quality and Dimension report.
MOQ: 1pcs.
Supplementary Technology: Brinell hardness, HBW according to EN ISO 6506-1, on a milled surface 0,5–2 mm below plate surface per heat and 40 tons. Tests are made for every variation of 15 mm in the thickness of plates from the same heat.
| Brand | C | Si | Mn | P | S | Cr | Mo | Ni | B | CEV |
| NM360 | ≤0.17 | ≤0.50 | ≤1.5 | ≤0.025 | ≤0.015 | ≤0.70 | ≤0.40 | ≤0.50 | ≤0.005 | |
| NM400 | ≤0.24 | ≤0.50 | ≤1.6 | ≤0.025 | ≤0.015 | 0.4~0.8 | 0.2~0.5 | 0.2~0.5 | ≤0.005 | |
| NM450 | ≤0.26 | ≤0.70 | ≤1.60 | ≤0.025 | ≤0.015 | ≤1.50 | ≤0.05 | ≤1.0 | ≤0.004 | |
| NM500 | ≤0.38 | ≤0.70 | ≤1.70 | ≤0.020 | ≤0.010 | ≤1.20 | ≤0.65 | ≤1.0 | Bt: 0.005-0.06 | 0.65 |
| Brand | Thickness mm | Tensile Test MPa | Hardness | |||||||
| YS Rel MPa | TS Rm MPa | Elongation % | ||||||||
| NM360 | 10-50 | ≥620 | 725-900 | ≥16 | 320-400 | |||||
| NM400 | 10-50 | ≥620 | 725-900 | ≥16 | 380-460 | |||||
| NM450 | 10-50 | 1250-1370 | 1330-1600 | ≥20 | 410-490 | |||||
| NM500 | 10-50 | --- | ---- | ≥24 | 480-525 | |||||
Capacity: 3,000 ton per month.
Test: Chemical analysis, Metallographic, Mechnical analysis, Ultrasonic testing, Impact testing, Hardness testing, Surface quality and Dimension report.
Package: Bundle or piece.
Mill’s Test Certificate
EN 10204/3.1 with all relevant data reg. chem. composition, mech. properties and results of testing.
Heat treatment: quenching and tempering (quenching and tempering).
NM500 wear-resistant steel is widely used construction machinery, mining machinery, mining machinery, environmental protection machinery, metallurgical machinery, abrasives, bearings and other product components.