Heat Resistant 310H Stainless Steel Plate AISI310H 3.0 - 40.0mm in 1500mm Width from TISCO
More Informations of our Products
Product | Stainless Steel Sheet/Plate |
Standard | ASTM A240,GB/T3280-2007,JIS4304-2005,ASTM A167,EN10088-2-2005,etc |
Material | 310S,310,310H,309,309S,316,316L,316Ti,317,317L,321,321H,347,347H,304,304L,302,301, 201,202,403,405,409,409L,410,410S,420,430,631,904L,Duplex,etc |
Surface | 2B,2D,BA,NO.1,NO.4,NO.8,8K,mirror,checkered,embossed,hair line,sand
blast,Brush |
Thickness | Cold Rolled:0.3-6mm |
Hot Rolled: 3-20mm | |
Width | 1000mm,1219mm,1500mm,1800mm,2000mm,2500mm,,etc |
Length | 2000mm,2440mm,3000mm,5800mm,6000mm,etc |
Package | Covered with a layer of plastic film and cardboard,packed on the
wooden pallets/ iron packing,bound with iron belt,loaded in the
containers. |
Price Terms | Ex-Work,FOB,CFR,CIF,FCA,etc |
Payment Terms | TT,L/C at sight ,western Union,etc. |
Stainless steel grade 310H has carbon content and is a preferred choice for high temperature applications. This steel has good resistance to oxidation at temperatures of up to 1040°C (1904°F) in intermittent service and 1150°C (2102°F) in continuous service. It is widely used in environments where sulfur dioxide gas is present at high temperatures; however it is recommended that this steel should not be continuously used at 425-860°C (797-1580°F) range due to carbide precipitation.
The following datasheet provides an overview of stainless steel grade 310H.
310H Stainless Steel Plate We Have Stock
| 3.0*1500*6000mm | 4.0*1500*6000mm | 5.0*1500*6000mm | 6.0*1500*6000mm |
| 8.0*1500*6000mm | 10.0*1500*6000mm | 12.0*1500*6000mm | 14.0*1500*6000mm |
| 15.0*1500*6000mm | 16.0*1500*6000mm | 18.0*1500*6000mm | 20.0*1500*6000mm |
| 22.0*1500*6000mm | 25.0*1500*6000mm | 30.0*1500*6000mm | 32.0*1500*6000mm |
| 35.0*1500*6000mm | 38.0*1500*6000mm | 40.0*1500*6000mm |
The chemical composition of grade 310H stainless steel is outlined in the following table.
| Element | Content (%) |
|---|---|
| Iron, Fe | 49.075-45.865 |
| Chromium, Cr | 24-26 |
| Nickel, Ni | 19-22 |
| Manganese, Mn | 2 |
| Silicon, Si | 0.75 |
| Phosphorous, P | 0.045 |
| Carbon, C | 0.040-0.10 |
| Sulfur, S | 0.03 |
The mechanical properties of annealed grade 310H stainless steel are displayed in the following table.
| Properties | Metric | Imperial |
|---|---|---|
| Tensile strength | 515 MPa | 74694 psi |
| Yield strength | 205 MPa | 29732 psi |
| Modulus of elasticity | 200 GPa | 29000 ksi |
| Shear modulus | 77.0 GPa | 11200 ksi |
| Poissons ratio | 0.3 | 0.3 |
| Elongation at break (in 50 mm) | 40% | 40% |
| Hardness, Rockwell B | 95 | 95 |
| Hardness, Brinell | 217 | 217 |
Grade 310H stainless steel is chiefly used in the heat treatment industry, and the chemical process industry.
The following are the specific areas of applications: