ASTM A240 301 Stainless Steel Strip 1mm 1/4H 1/2H 3/4H FH

Country/Region	china
City & Province	wuxi jiangsu
Categories	Nickel

Product Details

ASTM A240 301 Stainless Steel Strip 1/4H 1/2H 3/4H FH Stainless Steel Coil & Foil Thickness 0.1 - 2.0mm

ProductName:	AISI 201 202 301 304 310 316 316L Surface 2b, Ba, Hairline, No.4, 8K, Mirror Finish Stainless Steel Cold Rolled Strip for Sale
Standard:	ASTM,AISI,DIN,EN,GB,JIS
Grade:	201,304,310S,316,316L,430,409,410
Thickness:	0.15mm-3.0mm
Width:	15mm-1500mm,or customized
Edge:	Slit edge/Mill edge
Surface:	2B,BA,HL,Mirror,2D,NO.1
Packaging:	Standard exporter package or as your requirements
Origin:	Foshan, China (Mainland)
Supply Ability:	5000 Tons per Month
Price terms:	EX-Work,FOB,CIF,CFR,CNF
Payment terms:	T/T,30%advanced payment before production and balance before shipment; OR Irrevocable L/C at sight.
MOQ:	FCL, 25 metric tons per 20 GP, can be assorted with different sizes. LCL for trial order is acceptable.
Delivery time:	10-15 days after receiving deposit by T/T or L/C.
Sample:	Samples free and express charges bear by you.

Datasheet & Specification

The following tables and lists give the stainless steel 301 datasheet and specification including chemical composition, physical properties and mechanical properties, heat treatment, welding, etc.

Grade Specification

STANDARD	WERKSTOFF NR.	UNS	JIS	AFNOR	BS	GOST	EN
SS 301	1.4571	S31635	SUS 301	Z6CNDT17‐12	320S31	08Ch17N13M2T	X6CrNiMoTi17-12-2

Chemical Composition

SS 301 material chemical composition is listed in the following table.

Datasheet 1, The table below shows AISI 301 stainless steel composition.

SS 301 Chemical Composition, %
ASTM / SAE Type	AISI (UNS)	C, ≤	Si, ≤	Mn, ≤	P, ≤	S, ≤	Cr	Ni	Mo, ≤	Cu, ≤	N, ≤
ASTM 666; ASTM A959; ASTM A240/A240M; SAE J405	301 (UNS S30100)	0.15	1.00	2.00	0.045	0.03	16.0-18.0	6.0-8.0	–	–	0.1
SAE AMS 5517	18Cr-8Ni (SAE 30301)	0.15	1.00	2.00	0.040	0.03	16.0-18.0	6.0-8.0	0.75	0.75	–

Notes:

ASTM 666: Standard Specification for Annealed or Cold-Worked Austenitic Stainless Steel Sheet, Strip, Plate, and Flat Bar
ASTM A240/A240M: Chromium and Chromium-Nickel Stainless Steel Plate, Sheet, and Strip for Pressure Vessels and for General Applications
ASTM A959: Standard Guide for Specifying Harmonized Standard Grade Compositions for Wrought Stainless Steels
SAE AMS 5517: Steel, Corrosion Resistant, Sheet and Strip
SAE J405: Chemical Composition of SAE Wrought Stainless Steels

PROPERTIES: ANNEALED CONDITION

Ultimate Tensile Strength: 75 KSI min (930 MPA min) Yield Strength: (0.2% offset): 30 KSI min (205 MPA min) Elongation: 40% Min Hardness: B92 or Equiv. Max

Temper	Tensile Strength	Yield Strength (0.2% Offset)	Elongation	Min Hardness
Annealed	75 KSI min	30 KSI min / 205 MPA min	40% Min	B92 or Equiv. Max

PROPERTIES: TEMPERED

Temper	Tensile Strength	Yield Strength (0.2% Offset)	Elongation
1/16 Hard	90 KSI min	55 KSI min / 380 MPA min	40% Min
1/8 Hard	100 KSI min	55 KSI min / 380 MPA min	40% Min
1/4 Hard	125 KSI min	55 KSI min / 380 MPA min	25% Min
1/2 Hard	150 KSI min	110 KSI min / 760 MPA min	15% < .015" 18% > .015"
3/4 Hard	175 KSI min	135 KSI min / 930 MPA min	10% < .015" 12% > .015"
Full-Hard	185 KSI min	140 KSI min / 965 MPA min	8% < .015" 9% > .015"
Super Full-Hard	270 KSI min	260 KSI min	Report for all thicknesses

1/16 Hard

Ultimate Tensile Strength: 90 KSI min (629 MPA min)
Yield Strength: (0.2% Offset) 45 KSI min (310 MPA min)
Elongation: 40% Min

1/8 Hard

Ultimate Tensile Strength: 100 KSI min (690 MPA)
Yield Strength: (0.2% Offset) 55 KSI min/380 MPA min
Elongation: 40% Min

1/4 Hard

Ultimate Tensile Strength: 125 KSI min (860 MPA) Yield Strength: (0.2% Offset) 75 KSI min/930 MPA min Elongation: 25% Min

1/2 Hard

Ultimate Tensile Strength: 150 KSI min (1035 MPA min)
Yield Strength: (0.2% Offset) 110 KSI min (760 MPA min)
Elongation: 15%<.015" 18%>.015"

3/4 Hard

Ultimate Tensile Strength: 175 KSI min (1205 MPA min)
Yield Strength: (0.2% Offset) 135 KSI MIN/930 MPA MIN
Elongation: 10%< .015" 12%> .015"

Full Hard

Ultimate Tensile Strength: 185 KSI min (1275 MPA min)
Yield Strength: (0.2% Offset) 140 KSI min (965 MPA min)
Elongation: 8% < .015" 9% > .015"

Super Full Hard

Ultimate Tensile Strength: 270 KSI min< .014" (1860 MPA min) 250 KSI min .015" to 017" (1720 MPA min) 225 KSI min .0171" to .019" (1552 MPA min) 205 KSI min .0191 to .021 (1435 MPA min) 185 KSI min >.0211 (1275 MPA min)