EN 1.4841 Stainless Steel Plate 0.6 - 30.0mm AISI314 Stainless Steel Sheet & Plate Baosteel
Specification of our EN 1.4841 Stainless Steel Plate
| Products | EN1.4841 Stainless Steel Plate Sheet |
| Thickness | cold rolled 0.4 - 5.0mm |
| hot rolled 3.0 - 100mm | |
| Width | cold rolled 1000mm 1219mm 1500mm |
| hot rolled 1500mm 1800mm 2000mm | |
| Surface | 2B BA NO.1 NO.4 8K HL |
| Brand | TISCO BAOSTEEL POSCO JISCO |
| Equal Grade | 1.4841 / 310Si2 / X8CrNiSI25-21 |
| Other Grade | 201 202 304 309S 310S 316L 321 347 410 420 430 2205 2507 904L 254SMO.etc |
| Standard | EN 10088-2 ASTM A240 JIS G4303 |
| Service | Cutting , Surface Finishing |
| MOQ | 500 kgs |
| Packing | Wooden pallets and waterproof paper |
| Loading Port | Shanghai Port,China |
| FCL Qty | 25 Tons each 20ft and 40ft container |
Austenitic steels such as 1.4841 have only 30% of the thermal conductivity of unalloyed steels. Their melting point is lower than that of unalloyed steels, so austenitic steels must be welded with lower heat input than unalloyed steels. In order to avoid overheating or burn-through with thinner sheets, high welding speeds must be used. Grade 1.4841 is suitable for components that need to be scale resistant up to about 1150 °C.
1.4841 is a heat resistant steel which has its origins in 1.4828, but which is much more stable at high temperatures due to its higher chromium and nickel content to oxidation. This steel is characterized by its good mechanical properties at high temperatures and is therefore particularly suitable where great value is placed on good mechanical properties at high temperatures.
| Material Designation | 1.4841 |
| AISI/SAE | 314 / 314L |
| EN Material Symbol | X15CrNiSi25-20 |
| UNS | S 31400 |
| Registered Trademark | Cronifer®2520 |
| AFNOR | Z 15 CNS 25-20 |
| Norm | DIN EN 10095, SEW 470 |
| Proof stress Rp0,2 MPa min. | Tensile strength Rm MPa | Elongation at fracture A80 % min. |
| 230 | 550-750 | 28 |
| Percentage by weight % max. | |||||||
| C | Cr | Ni min. | N | Si | Mn | P | S |
| 0.20 | 24.0-26.0 | 19.0-22.0 | 0.11 | 1.50-2.50 | 2 | 0.045 | 0.015 |
Typical areas of application for 1.4841Stainless Steel are:
The material 1.4841 is characterized by the following features: