ASTM A240/240M UNS S32205 Duplex Stainless Steel Plate Thickness 3.0 - 16.0mm Custom Cutting SS Plate
Specification of our 2205 duplex stainless steel plate
| Product Name | duplex 2205 Stainless Steel Plate/Sheet |
| Technical Standard | JIS,AISI, ASTM,GB,DIN,EN |
| Steel Grade | 2205 / S32205 / S31803 / 1.4462 |
| Type | Stainless steel sheet/ plate/coil |
| Thickness | Cold rolled:0.4~3.0mm |
| Hot rolled:3mm~100mm | |
| Width | 1000mm 1219mm 1500mm 2000mm or custom cutting as request |
| Length | custom as clients request |
| Surface | NO.1 2B or process other finishing |
| QualityCertificate | Mill Test Certificate |
| Package | Water proof paper is inner packing,galvanized steel or coated steel sheet is outer packing , side guard plate,then wrapped by seven steel belt.or according to customer's requirement |
| Trade term | FOB CIF CFR |
| Loading port | Shanghai Port, China |
Alloy 2205 duplex stainless steel is an alloy developed from the initial Super Duplex Stainless Steel. It is supplied in the solution annealed condition.
As a form of duplex stainless steel, alloy 2205 was designed as comprising 22% chromium, 3% molybdenum, and 5-6% nickel nitrogen. Alloy 2205 combines the desirable aspect of properties of both austenitic and ferritic grades. The high chromium, molybdenum and nitrogen mixture results in a Pitting Resistance Equivalent number (PREN) of 33-34, providing pitting and crevice corrosion resistance superior to Alloy 316L or Alloy 317L austenitic stainless steels in almost all corrosive media.
As a result of its excellent corrosion properties, it is well-suited to environments containing chlorides and hydrogen sulphide, for use in oil and gas extraction from sour wells, in refineries and in process solutions contaminated with chlorides.
It also has good erosion fatigue properties as well as lower thermal expansion and higher thermal conductivity than austenitic steels. The yield strength is about twice that of austenitic stainless steels, allowing a designer to save weight and make the alloy more cost-competitive when compared to Alloy 316L or Alloy 317L.
Composition ranges for 2205 grade stainless steels
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | N | |
| 2205 (S31803) | Min Max | - 0.030 | - 2.00 | - 1.00 | - 0.030 | - 0.020 | 21.0 23.0 | 2.5 3.5 | 4.5 6.5 | 0.08 0.20 |
| 2205 (S32205) | Min Max | - 0.030 | - 2.00 | - 1.00 | - 0.030 | - 0.020 | 22.0 23.0 | 3.0 3.5 | 4.5 6.5 | 0.14 0.20 |
| Grade | Tensile Str (MPa) min | Yield Strength 0.2% Proof (MPa) min | Elongation (% in 50mm) min | Hardness | |
| Rockwell C (HR C) | Brinell (HB) | ||||
| 2205 | 621 | 448 | 25 | 31 max | 293 max |
Grade specification comparisons for 2205 grade stainless steels
| Grade | UNS No | Old British | Euronorm | Swedish SS | Japanese JIS | ||
| BS | En | No | Name | ||||
| 2205 | S31803 / S32205 | 318S13 | - | 1.4462 | X2CrNiMoN22-5-3 | 2377 | SUS 329J3L |