DIN 11850 Grade 1.4301 85 X 2.0MM Welded Stainless Steel Tube OD
DIN EN 1.4301 material (steel name is X5CrNi18-10) is a universal
austenitic stainless steel with good resistance to atmospheric,
organic and inorganic chemicals. It is widely used due to its
excellent intergranular corrosion resistance, good cold
deformability, good deep drawability and weldability.
DIN EN 1.4301 stainless steel has good atmospheric corrosion
resistance up to 300 °C, and good resistance to many (lightly
corrosive) organic and inorganic chemicals. It can also be used at
very low temperatures, but there are some limitations in marine,
coastal and chloride-containing solutions.
EN X5CrNi18-10 is non-magnetic in the annealed state, but it may
become slightly magnetic due to the addition of martensite or
ferrite during cold working or welding.
|Standard:||EN10217-7, DIN 11850|
|Finish:||BA / Bright Annealed. OD Polished|
|Mill Test Certificate:||EN10204 3.1|
|Packing:||Sleeved, Wooden Boxed|
Chemical Composition 1.4301 Welded Stainless Steel Tube:
|Chemical Element||% ( Weight )|
|Carbon (C)||0.0 - 0.08|
|Chromium (Cr)||17.500 - 19.50|
|Manganese (Mn)||0.0 - 2.00|
|Silicon (Si)||0.0 - 1.00|
|Phosphorous (P)||0.0 - 0.05|
|Sulphur (S)||0.0 - 0.03|
|Nickel (Ni)||8.00 - 10.50|
|Nitrogen (N)||0.0 - 0.11|
Mechanical Property 1.4301 Welded Stainless Steel Tube:
|Proof Stress||190 Min MPa|
|Tensile Strength||500 to 700 MPa|
|Elongation A50 mm||45 Min %|
|Hardness Brinell||215 Max HB|
Available Tube Product Forms:
Due to its good corrosion resistance, processability and
weldability, EN 1.4301 stainless steel is widely used in chemical,
tableware, watches, auto parts, medical equipment, architectural
decoration, aerospace and electrical appliances.
Spezilla's 1.4301 welded stainless steel tubes are produced
acc. to the following process and inspection to assure our quality:
1. Chemical Composition Analysis Test With 100% PMI.
2. Solution Annealing / Bright Annealed.
3. 100% Hydrostatic Test and 100% Eddy Current Test
4. Mechanical Tests includes Tension Test, Flattening Test, Flaring
Test, Hardness Test.
5. Impact Test subject to Standard request.
6. Grain Size Test and Intergranular Corrosion Test.
7. Visual Test and Endoscope Test for Surface Quality Test
Typical Manufacturing Specifications:
Also individual customer specifications.