ASME SB111 heat exchanger steel tube, Copper Nickel Alloy Pipe C71500 6096MM Length
Description:
Applications:
Underwater fencing
Sugar plants
Air conditioners
Refrigeration
Oil lines
Gas lines
Industrial machinery
Plumbing
Machinery &equipment
Heat exchanger tubes
Steam tubes
Power plants
Ship building & ship repairs
Condensers
Distillers
Evaporators
Ferrules
Plumbing flanges
Power steering tubes
Salt water piping systems
| Standard Grade | ASTM B 111 C71500 | EN 12451 CuNi30Mn1Fe (CW354H) | DIN 17664/1785 CuNi30Mn1Fe | BS 2871 Part 3 CN 107 | NFA 51102 CuNi30Mn1Fe | JIS H3300 C7150 |
| Cu | Rem. | Rem. | Rem. | Rem. | Rem. | Rem. |
| Pb | 0,05 max. | 0,02 max. | 0,03 max. | 0,01 max. | 0,05 Sn+Pb max. | 0,05 max. |
| Ni | 29,0 - 33,0 | 30,0 - 32,0 | 30,0 - 32,0 | 30,0 - 32,0 | 29,0 - 32,0 | 29,0 - 33,0 |
| Fe | 0,4 - 1,0 | 0,4 - 1,0 | 0,4 - 1,0 | 0,4 - 1,0 | 0,4 - 0,7 | 0,4 - 0,7 |
| Mn | 1,0 max. | 0,5 - 1,5 | 0,5 - 1,5 | 0,5 - 1,5 | 0,5 - 1,5 | 0,2 - 1,0 |
| Zn | 1,0 max. | 0,5 max. | 0,5 max. | - | 0,5 max. | 0,5 max. |
| S | - | 0,05 max. | 0,06 max. | 0,08 max. | 0,02 max. | - |
| Sn | - | 0,05 max. | - | - | - | - |
| P | - | 0,02 max. | - | - | - | - |
| C | - | 0,05 max. | 0,06 max. | 0,06 max. | 0,06 max. | - |
| Co | - | 0,1 max. | - | - | - | - |
| Cu+Ni+Fe+Mn | - | - | - | - | - | 99,5 min. |
| Total Impurities | - | Others Total | Others Total | 0,3 max. | 0,1 max. | - |
| - | 0,2 max. | 0,1 max. | - | - | - | |
| Condition | O61 | R370 | F37 | M | annealed (X690) | O |
| HR50 | R480 | - | O | - | - | |
| - | - | - | - | - | - | |
| Yield Strength | 125 min. | 120 min. | 120 - 220 | - | - | - |
| N/mm² | 345 min. | 300 min. | - | - | - | - |
| - | - | - | - | - | - | |
| Tensile Strength | 360 min. | 370 min. | 370 min. | - | - | 363 min. |
| N/mm² | 495 min. | 480 min. | - | - | - | - |
| - | - | - | - | - | - | |
| Elongation (%) | - | 35 min. | 35 min. | - | - | 30 min. |
| 12 min. (WT<1,21 mm) | 12 min. | - | - | - | - | |
| 15 min. (WT>1,21 mm) | - | - | - | - | - | |
| Hardness Hv5 | - | - | - | 150 min. | 90 - 130 | - |
| - | - | - | 90 - 120 | - | - | |
| - | - | - | - | - | - | |
| Grain Size (mm) | 0,010 - 0,045 | 0,010 - 0,050 | 0,010 - 0,050 | 0,050 max. | 0,010 - 0,045 | 0,010 - 0,045 |
| - | (annealed) | - | (Condition O) | - | - | |
| Typical use: | This alloy has all the characteristics of CuNi 90/10, but also
offers excellent corrosion resistance in high velocity sea water.
Also the operating temperature is much higher than of CuNi 90/10.
Can assure a long service life and reliability. Melting Point: 1240°C • Hot Working Properties: Good Density (20°C): 8,94 g/cm³ • Cold Working Properties: Good | |||||
| Weight formula: | Average Wall: Minimum Wall: | (OD-WT) x WT x 0,0284 = Kg/m (all sizes in mm) (OD-WT) x WT x 0,0295 = Kg/m (all sizes in mm) | ||||