ASTM 201 No.1 Finish Hot Rolled Stainless Steel Sheet 4mm Thickness SS Plate
The circulation of 201 stainless steel on the market, nickel content from 0.5 to 5 nickel, according to the requirements of the use of the component difference. This type of steel is mainly used to replace 304 stainless steel in some specific uses. Steel 201 contains manganese, which rusts in humid and salty air for a long time.
Product introduction:
| Commodity | ASTM 201 No.1 Finish Hot Rolled Stainless Steel Sheet 4mm Thickness SS Plate |
| Grade | 201 |
| Brand | HONGWANG DELONG |
| Certification | SGS,BV,IQI,TUV,ISO,etc |
| Thickness | 4mm |
| Width | 1000 1219 1500mm or as customer's requirments |
| Length | 2000 3000 6000 mm or as customer's requirments |
| Surface | nO.1 |
| Standard | JIS,AISI,ASTM,GB,DIN |
| Delivery time | About 15 -30 days or based on the sales contract |
| MOQ | 1 Ton |
| Advantages | Widely used in kithenware, water ware,general use |
Product Display :
Comparing to 304 :
Due to the relationship between the manganese element, the color will be darker than 304 steel, but it is
difficult to distinguish with the naked eye. Because the nickel content is different, the corrosion resistance
of 201 is not as good as 304, and the higher carbon content makes 201 stainless steel harder and more
brittle than 304.
Chemical Composition:
| Grade | C | Si | Mn | P | S | Ni | Cr | |
| 201 | ≤0.15 | ≤1.00 | 5.5-7.50 | ≤0.045 | ≤0.03 | 0.50-1.0 | 1600～18.00 |
Physical Property:
| Grade | Tensile Strength(Mpa) | Yield Strength(Mpa) | Elongation(%) | HBW | HRB | HV | Density |
| 201 | ≥520 | ≥275 | ≥40 | ≤187 | ≤90 | ≤200 | 7.93g/cm |
Surface Finish:
| Surface Finish | Definition | Application |
| 2B | Finished by heat treatment, pickling after cold rolling. Followed by skin pass line to be more brighter and smooth surface | General application Medical instruments, Tableware |
| BA | Bright heat treament after cold rolling | Kitchen utensil, kitchenware, architectural |
| 8K | A mirror-like reflective surface by polishing with finer abrasives over 800mesh | Construction, mirrors, plate sets, decoration elevators |
| HL | Finished by continuous linear polishing | Architectural purpose, Escalators, kitchenware, vehicles |
| NO.1 | Finished by hot rolling, annealing and picking, characterized by white pickled surface | Chemical industry Equipment, industrail tanks |
| NO.4 | Polishing with NO.150 to NO.180 mesh abrasives specified in JISR6001 | Kitchen utensils, Building Construction, Medical equipment |