DX51d 0.18mm 2mm Galvanised Sheet Hot Dip Slightly Oiled ISO9001
Hot-dip galvanized steel sheet. The thin steel plate is immersed in
the molten zinc tank, so that a thin steel plate with a layer of
zinc is adhered to the surface. At present, it is mainly produced
by continuous galvanizing process, that is, continuous immersion of
rolled steel sheets in a galvanizing tank with molten zinc to make
galvanized steel sheets; alloyed galvanized steel sheets. This kind
of steel plate is also manufactured by hot dipping, but immediately
after it is discharged from the tank, it is heated to about 500°C
to form an alloy film of zinc and iron. This kind of galvanized
sheet has good paint adhesion and weldability; electro-galvanized
steel sheet. The galvanized steel sheet produced by the
electroplating method has good workability. |
Specfications
Chemical Composition
| Specification | Grade | Chemical Composition(wt%) | ||||||
| C | Mn | Ni | Cr | Mo | Ti | |||
| ASTMJIS | 316L/022Cr17Ni12Mo2 | ≤0.03 | ≤2.0 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | - | |
| JIS | SUS316L | ≤0.03 | ≤2.0 | 12.0-15.0 | 16.0-18.0 | 2.0-3.0 | - | |
| ASTMJIS | 316Ti/SUS 316Ti | ≤0.08 | ≤2.0 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | 5*(C+N)-0.7 | |
Properties
| Spec | Grade | Mechanical Property | Physical Property | ||||
Y.S (N/MM2) | T.S (N/MM2) | EL (%) | HRB | Specific Heat (J/g℃) | Modulus of Elasticity (KN/mm2) | ||
| ASTM/GB | 316L/022Cr17Ni12Mo2 | ≥170 | ≥485 | ≥40 | ≤95 | 0.5 | 193 |
| JIS | SUS316L | ≥175 | ≥480 | ≥40 | ≤90 | 193 | |
| ASTM | 316Ti | ≥205 | ≥515 | ≥40 | ≤95 | 0.5 | 200 |
Applications:316L: Widely used in corrosion-susceptible environment and some mechanical components those are difficult to make heat treatment after forming in more corrosive environment.
316Ti: Mainly used for industrial components.
|