Active Member
|
[China]
Address: Room 1514, Floor 4, No. 111, Fengpu Avenue, Fengpu Industrial Zone, Fengxian District, Shanghai, China
Contact name:camille
Shanghai Nadong Metal Products Co.,Ltd. |
|
|
Hot-dip galvanized steel pipe is an alloy layer formed by the reaction of molten metal and iron matrix, thereby bonding the matrix and coating together. Hot dip galvanizing is a process of pickling steel pipes. In order to remove the iron oxide on the surface of the steel pipe, after pickling, the steel pipe is cleaned with an ammonium chloride or zinc chloride aqueous solution or a mixed aqueous solution of ammonium chloride and zinc chloride, and then sent to a hot-dip galvanizing tank. |
| Product Name | Hot Dipped Galvanized Steel Tube / Cold Roleld Pre Galvanized Pipe / Galvanized Tube |
| Material | Q195 Q235 Q345 |
| Wall Thickness | 1MM~12MM |
| Size | 10MMX10MM~600MM~600MM |
| Length | Length:Single random length/Double random length 5m-14m,5.8m,6m,10m-12m,12m or as customer's actual reques |
| Standard | ASTM A53,BS1387-1985,GB/T3091-2001,GB/T13793-92, GB/T6728- 2002,API 5L |
| Packing | Bundle, or with all kinds of colors PVC or as your requirements |
| Pipe Ends | Plain end/Beveled,protected by plastic caps on both ends, cut quare,grooved,threaded and coupling,etc. |
| Surface Treatment | 1. Galvanized 2. PVC,Black and color painting 3. Transparent oil,anti-rust oil 4. According to clients requirement |
| Product Application | 1. Fence, greenhouse, door pipe,greenhouse 2. Low pressure liquid, water, gas, oil, line pipe 3. For both indoor and outdoor the building construction 4. Widely used in scaffolding construction which is much cheaper and convenient |
| Origin | Tianjin China |
| Certificates | API ISO9001-2008,SGS.BV,API, |
| Delivery Time | Usually within 10-45 days after receipt of advance payment |
Chemical Composition
| Specification | Grade | Chemical Composition(wt%) | ||||||
| C | Mn | Ni | Cr | Mo | Ti | |||
| ASTMJIS | 316L/022Cr17Ni12Mo2 | ≤0.03 | ≤2.0 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | - | |
| JIS | SUS316L | ≤0.03 | ≤2.0 | 12.0-15.0 | 16.0-18.0 | 2.0-3.0 | - | |
| ASTMJIS | 316Ti/SUS 316Ti | ≤0.08 | ≤2.0 | 10.0-14.0 | 16.0-18.0 | 2.0-3.0 | 5*(C+N)-0.7 | |
Properties
| Spec | Grade | Mechanical Property | Physical Property | ||||
Y.S (N/MM2) | T.S (N/MM2) | EL (%) | HRB | Specific Heat (J/g℃) | Modulus of Elasticity (KN/mm2) | ||
| ASTM/GB | 316L/022Cr17Ni12Mo2 | ≥170 | ≥485 | ≥40 | ≤95 | 0.5 | 193 |
| JIS | SUS316L | ≥175 | ≥480 | ≥40 | ≤90 | 193 | |
| ASTM | 316Ti | ≥205 | ≥515 | ≥40 | ≤95 | 0.5 | 200 |
Applications:316L: Widely used in corrosion-susceptible environment and some mechanical components those are difficult to make heat treatment after forming in more corrosive environment.316Ti: Mainly used for industrial components. |