AMS 5661 Turbine Blade Steel UNS N09901 Solid Square Bar
Production Information
Alloy 901 is an age-hardenable super alloy which contains Titanium and Aluminium for precipitation hardening and molybdenum for soild-solution strengthening. Alloy 901 has high yield strength and creep at temperatures around 1110°F (600°C). Alloy 901 is able to combine strength with good forging characteristics due to its high iron content. Alloy 901 is commonly used in gas turbine engine discs, shafts, rings, bushings and seals.
Size Range
Round bar / Wire rod (Diameter): | 3.0mm to 900mm |
Square bar / Flat bar: | 5.0mm to 1100mm |
Forging piece: | Stepped shafts with flanks / discs /tubes |
Heavy/middle plate via hot rolled: | T6 - 100mm X W10 - 1300mm X L1000-10000mm |
Sheet steel via cold rolled: | T0.5 - 5.5mm X W6 - 1000mm X L1000 - 11000mm |
Steel strip via cold rolled: | T0.1 - 5.0mm X W5 - 150mm X L (or in coil form) |
Length | Fixed length or random length or based on the customer's special requirement. |
Chemical Composition and standard
Grade | AMS 5661E |
standard | SAE AMS 5661E-1995 |
Chemical Composition (weight%) | C (%): ≤ 0.10
B (%): 0.010 ~ 0.020 Mn (%): ≤ 1.00 Cu (%): ≤ 0.50 Si (%): ≤ 0.60
Co (%): ≤ 1.00 P (%)≤: 0.030 Pd (%): ≤ 5 ppm S (%)≤: 0.030 Bi (%): ≤ 0.3 ppm Cr (%): 11.0 ~ 14.0 Fe (%): balance Ni (%): 40.0 ~ 45.0 Mo (%): 5.00 ~ 7.00 Ti (%): 2.35 ~ 3.10 Al (%): ≤ 0.35 |
Mechanical Properties
AMS 5661 Stainless Steel Mechanical Properties
Tensile strength,Rm/MPa: | ≥1138 |
Yield strength,Rp/MPa: | ≥827 |
Elongation/%: |
≥12
|
Reduction of area, ψ/%: |
≥15
|
Impact, KV /J: | -- |
Annealed hardness HBS: | 302~388 |