15-5PH Turbine Blade Steel 15-5PH Round Bar 15-5PH Flat Bar 15-5PH Bar
Description
Our company provides 15-5PH Turbine Blade Steel Hot rolled steel products / Hot rolled wire rods 15-5PH Round Bar 15-5PH Hot rolled round bars / Hot rolled flat bars.
All of 15-5PH Turbine Blade Steel Hot rolled steel products / Hot rolled wire rods 15-5PH Round Bar 15-5PH Hot rolled round bars / Hot rolled flat bars. conform to Military standard, nuclear power. 100% Ultrasonic test ASTM E2375 /SAE AMS 2154 /SEP 1923 /GB/T 4162 /EN 10228-3.
Products Details
15-5PH Turbine Blade Steel Hot rolled steel products / Hot rolled wire rods 15-5PH Round Bar 15-5PH Hot rolled round bars / Hot rolled flat bars.
| Chemical Composition (weight%): | C (％): ≤ 0.07 |
| Si (％): ≤ 1.00 | |
| Mn (％): ≤ 1.00 | |
| P (％)≤: 0.040 | |
| S (％)≤: 0.030 | |
| Cr (％): 14.0 ~ 15.5 | |
| Ni (％): 3.50 ~ 5.50 | |
| Mo (％): - | |
| Cu (％): 2.50 ~ 4.50 | |
| Nb+Ta (%): 0.15 ~ 0.45 | |
| Mechanical Properties Under Final Heat Treatment: | Form: Bar, forge piece |
| Condition: H900 | |
| Tensile strength, σb/MPa: 1310 | |
| Yield strength, σ0.2/MPa: 1170 | |
| Elongation, δ (％): 10.0 | |
| Reduction of area, ψ (％): 35 | |
| Harndess: HRC: ≥ 40 | |
| Form: Bar, forge piece | |
| Condition: H925 | |
| σb/MPa: 1170 | |
| σ0.2/MPa: 1070 | |
| δ (％): L-10.0 | |
| ψ (％): L-38.0 | |
| Hardness HRC: ≥ 38 | |
| Form: Bar, forge piece | |
| Condition: H1025 | |
| σb/MPa: 1070 | |
| σ0.2/MPa: 1000 | |
| δ (％): 12.0 | |
| ψ (％): 45 | |
| Hardness HRC: ≥ 35 | |
| Form: Bar, forge piece | |
| Condition: H1075 | |
| σb/MPa: 1000 | |
| σ0.2/MPa: 860 | |
| δ (％): 13.0 | |
| ψ (％): 45.0 | |
| Hardness HRC: ≥32 | |
| Form: Bar, forge piece | |
| Condition: H1100 | |
| σb/MPa: 965 | |
| σ0.2/MPa: 795 | |
| δ(％): 14；10 | |
| ψ(％): 45；29 | |
| HRC: ≥31 |
15-5PH Turbine Blade Steel Heat treatment is only suitable for specific grades of stainless steel. When heat treating a stainless the hardening temperatures, including rate of heating, cooling and soaking times will vary due to several factors such as the shape and size of each component.
15-5PH Turbine Blade Steel XM-12 Round Bar AMS 5659 Flat Bar UNS S15500 Bar 1.4542 X5CrNiCuNb16-4
FAQ
Q: How do you control the quality?
A: We have professional inspectors to analyze the chemical composition of 15-5PH Turbine Blade Steel 15-5PH Round Bar 15-5PH Flat Bar 15-5PH Bar and test the finished products in strict accordance with the standards stipulated in the contract. In this process, the inner and outer surfaces, the appearance of both ends, bending, set length, outer diameter and Wall thickness will be checked one by one. You can rest assured that all products you receive from us are reliable.
Q: Do you accept customization?
A: Yes. If you have special requirements for products or packaging,
we can make them for you.
Q: Can you accept trial orders?
A: Our MOQ is usually 1 ton. However, if you want to place an order
as the start of our cooperation, we can accept smaller quantities
at the first time. Of course, after the start, we will have further
and longer cooperation.
Q: How do I get samples?
A: Free samples are available for your inspection and testing,
DHL/FedEx/UPS accounts can be used for sampling, and the courier
fee is borne by you.