Wood Texture Stamp Mat Mold Making Two-Part Liquid Polyurethane Rubber
Product Description
Liquid polyurethane rubber consists of A&B component, B is curing agent, and A is polyurethane prepolymer. It can also be used as a concrete or cement stamping mold as well as for making hard durable rubber parts for machinery or automotive applications.
Features
Non-yellowing urethane casting resins for applications demanding
optically clear castings
Mercury-free formulas available
Vacuum or pressure casting is recommended for bubble-free castings
Can be colored with color dyes to create clear, colored parts
Technical Datasheet
| A | Type | MCPU40 A | MCPU50 A | MCPU60 A | MCPU70 A | MCPU80 A | MCPU90 A |
| Appearance | Colorless or light yellow transparent liquid | ||||||
| Viscosity(30℃)mPa·s/ | 2500±300 | ||||||
| B | Type | MCPU40 B | MCPU50 B | MCPU60 B | MCPU70 B | MCPU80 B | MCPU90 B |
| Appearance | Light yellow liquid | ||||||
| Viscosity(30℃)/mPa·s | 560±200 | ||||||
| mix ratio | 1:1 | ||||||
| Appearance | Light yellow | ||||||
| Operation temperature/℃ | 25～40 | ||||||
| Gel time(30℃)*/min (variable) | 25-30 | 25-30 | 25-35 | 20-30 | 8-14 | 6-9 | |
| Hardness (shore A) | 40±3 | 50±3 | 60±3 | 70±3 | 80±3 | 90±3 | |
| Tensile strength/MPa | 4-7 | 5-8 | 5-8 | 8-11 | 9-14 | 18-25 | |
| Elongation at break/ % | 500-600 | 400-500 | 300-400 | 250-350 | 350-550 | 400-500 | |
| Tear strength/(kN/m) | 18-22 | 18-22 | 20-25 | 26-30 | 50-60 | 70-85 | |
| Rebound/ % | 30-35 | 30-35 | 30-35 | 30-35 | 36-40 | 32-35 | |
| Specific gravity(25℃)(g/ cm3) | 1.18 | ||||||
Applications
Substitute for making the industrial parts, It also applies to electrical equipment potting, rubber rollers, Ski and snowboard ,rubber plates, rubber wheels, shoe models and others.
Mixing:
Shake both A and B sides vigorously.
Measure out equal parts, by volume, of A and B into clean plastic
or metal containers.
Combine both sides into a third clean mixing container and mix
vigorously for at least one minute, taking care to scrape the sides
and bottom of the mixing container with your mixing utensil, until
the product is one uniform color.
Tips:
Always wear a respirator or self –contained breathing apparatus
when working with urethanes.
Use between 65F and 75F in a humidity-controlled environment.
AeroMarine Products Concrete Molding and Stamping Rubber 75A
Urethane is moisture sensitive.
Use only clean plastic and/or metal mixing utensils and containers.
Do not use paper or wood.
Re-cap the bottles immediately after use.
Extend-It aerosol nitrogen blanket can be used to protect the
product from moisture contamination.
Never mix less than about 3 ounces of product, as this ratio is
hard to measure and will take longer to cure as the exothermic
reaction does not generate much heat at this volume.
Avoid mixing with drill motors because of the friction they
generate, mixing with electric drills can start the exothermic cure
process and cause the product to cure in the mixing container.
It is always best to mix the material by hand, with a plastic or
metal mixing utensil.
Don’t vary the mix ratio. Unlike some polyester resins, altering
the mix ratio to vary the cure cycle will not work with urethanes.
Mix in clean plastic containers. Paper cups and wooden mixing
utensils may contain moisture which can adversely affect the
urethane rubber. Avoid waxed paper cups because the wax may melt
and contaminate the rubber.
Air bubbles in urethanes are almost always caused by moisture. Do
everything possible to avoid moisture getting into the mix. Replace
the lids onto the containers promptly after use. Do not use the
urethane rubber during rainy days or times of high humidity. Avoid
pouring against an unsealed water based product such as plaster or
hydrocal. Seal plaster or hydrocal with a product like Krylon Clear
Acrylic.
Avoid mixing a large batch- The larger the batch, the more exotherm
or heat is generated in the cure cycle. If you are making a large
mold, mix small batches to make the process more manageable.
Shake or stir well before use- The liquid components may settle in
the containers during storage. Shake or stir the components
separately and thoroughly before mixing. Let it sit a few minutes
to let any bubbles rise to the surface after shaking the container.
Package:20Kg/drum
Storage:Store in cool and dry place. If you can’t use one drum up at a time, please inject N2.The storage time of original packing is 6 months.