AISI H11 tool steel is a 5% chromium hot-work tool steel. Gnee steel supplies good quality H11 steel, and equivalents 1.2343/X37CrMoV5-1, SKD6, BH11 steel.AISI H11 Steel Round Bar Sheet Plate, DIN 1.2343, JIS SKD6 H11 steel also is called DIN 1.2343 and JIS SKD6 steel. 1.2343 steel is the air-cooling type hot work mold steel. It is one of the three most commonly used of hot work mold steel in the European die-casting industry. The carbide is small and distributed uniformly in steel.
| Diameter: | 10mm-1000mm (optional) |
| Length: | 1000mm-12000mm Straightness: 3mm/M max(optional) |
| Process: | Forged from vacuum degassed ingots. |
| Delivery condition: | Hot forged Rough machined (black surface after Q/T) Turned (optional) |
| Delivery Time: | 25 days |
| Heat treatment: | Normalized / Annealed / Quenched / tempered (optional) |
| Technical Data: | According to the customer's requirement of Chemical Composition, Physical Properties and Mechanical Testing |
| Properties: | As your request |
| Test: | Ultrasonic test according to SEP 1921-84 Class C/c and D/d (optional) |
| Marking: | Grade, heat NO. length will be stamped one each bar with required color |
| Payment: | 30% advance by TT, Balance pay before the shipment against shipping documents or irrevocable LC at sight |
Supply Form & Size & Tolerance
| Supply Form | Size(mm) | Process | Tolerance | |
Round | Φ6-Φ100 | Cold Drawn | Bright/Black | Best H11 |
Φ16-Φ350 | Hot Rolled | Black | -0/+1mm | |
| Peeled/ground | Best H11 | |||
Φ90-Φ1000 | Hot Forged | Black | -0/+5mm | |
| Rough Turned | -0/+3mm | |||
Flat/Square/Block | Thickness :120-800 | Hot Forged | Black | -0/+8mm |
| Width:120-1500 | Rough Machined | -0/+3mm | ||
Remark:Tolerance can be customized as per requests
Chemical Composition
| Standard | Grade | C | Si | Mn | P | S | Cr | V | Mo |
| ASTM A681 | H11 | 0.35-0.45 | 0.8-1.25 | 0.2-0.6 | 0.03 | 0.03 | 4.75-5.5 | 0.3-0.6 | 1.1-1.6 |
| DIN ISO 4957 | 1.2343 | 0.28-0.35 | 0.8-1.2 | 0.1-0.4 | 0.03 | 0.03 | 2.7-3.2 | 0.4-0.7 | 1.1-1.5 |
| JIS G4404 | SKD6 | 0.32-0.42 | 0.8-1.2 | 0.5 | 0.03 | 0.03 | 4.5-5.5 | 0.3-0.5 | 1.0-1.5 |
| BS 4659 | BH11 | 0.32-0.40 | 0.85-1.15 | 0.4 | 0.35 | 0.35 | 4.75-5.25 | 0.3-0.5 | 1.25-1.75 |
Physical Property
| Temperature | 20°C | 200°C | 400°C | 600°C |
| Density,kg/m3 | 7800 | 7750 | 7700 | 7600 |
| Modulus of elasticity,Mpa | 210000 | 200000 | 180000 | 140000 |
| Coefficient of thermal expansion from 20°C,per °C | — | 11.6 x 10^-6 | 12.4 x 10^-6 | 13.2 x 10^-6 |
| Thermal conductivity,W/m °C | — | 30 | 30 | 31 |
Mechanical Property
| Hardness,HRC | 45 | 46.5 | 48.5 |
| Tensile strength,Mpa | 1450 | 1580 | 1680 |
| Yield strength Rp 0.2,Mpa | 1240 | 1340 | 1410 |
| Elongation A5 ,% | 13 | 13 | 12 |
| Reduction in area Z,% | 65 | 65 | 64 |
Q: What is your time of making a sample
A: Usually we will take 1~3 days to make the sample
Q: What is your MOQ?
A: Usually 20 feet containers ( 25 tons) for section steel
Q: What is your delivery time?
A: For stocks, we can send the goods to loading port within 7 days
after receiving your deposit
For production period, it usually needs about 15days- 30 days after
receiving the deposit
Q: What is your service?
A: We will try our best to satisfy your per request.
We prepare to provide the pre-sales serves, service during sales
and afer-sales service for coustomes by the way of advance service,
value added service and personalized service.