Sabic Verton K3000Z resin is a compound based on Acetal resin containing Anti-Static. Added features of this material include: Antistat.
| TYPICAL PROPERTIES (1) | |||
| MECHANICAL | Value | Unit | Standard |
| Tensile Stress, yield | 41 | MPa | ASTM D 638 |
| Tensile Stress, break | 32 | MPa | ASTM D 638 |
| Tensile Strain, yield | 15.8 | % | ASTM D 638 |
| Tensile Strain, break | 59.5 | % | ASTM D 638 |
| Tensile Modulus, 50 mm/min | 1590 | MPa | ASTM D 638 |
| Flexural Stress | 49 | MPa | ASTM D 790 |
| Flexural Modulus | 1440 | MPa | ASTM D 790 |
| Tensile Stress, yield | 41 | MPa | ISO 527 |
| Tensile Stress, break | 36 | MPa | ISO 527 |
| Tensile Strain, yield | 13.3 | % | ISO 527 |
| Tensile Strain, break | 49.2 | % | ISO 527 |
| Tensile Modulus, 1 mm/min | 1500 | MPa | ISO 527 |
| Flexural Stress | 40 | MPa | ISO 178 |
| Flexural Modulus | 1500 | MPa | ISO 178 |
| IMPACT | Value | Unit | Standard |
| Izod Impact, unnotched, 23°C | NB | J/m | ASTM D 4812 |
| Izod Impact, notched, 23°C | NB | J/m | ASTM D 256 |
| Instrumented Impact Energy @ peak, 23°C | 28 | J | ASTM D 3763 |
| Multiaxial Impact | 16 | J | ISO 6603 |
| Izod Impact, unnotched 80*10*4 +23°C | NB | kJ/m² | ISO 180/1U |
| Izod Impact, notched 80*10*4 +23°C | 15 | kJ/m² | ISO 180/1A |
| THERMAL | Value | Unit | Standard |
| HDT, 0.45 MPa, 3.2 mm, unannealed | 146 | °C | ASTM D 648 |
| HDT, 1.82 MPa, 3.2mm, unannealed | 67 | °C | ASTM D 648 |
| CTE, -40°C to 40°C, flow | 1.3E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, xflow | 1.33E-04 | 1/°C | ASTM E 831 |
| CTE, -40°C to 40°C, flow | 1.3E-04 | 1/°C | ISO 11359-2 |
| CTE, -40°C to 40°C, xflow | 1.33E-04 | 1/°C | ISO 11359-2 |
| PHYSICAL | Value | Unit | Standard |
| Density | 1.32 | g/cm³ | ASTM D 792 |
| Moisture Absorption, 50% RH, 24 hrs | 2.29 | % | ASTM D 570 |
| Mold Shrinkage, flow, 24 hrs | 1.8 | % | ASTM D 955 |
| Mold Shrinkage, xflow, 24 hrs | 1.8 | % | ASTM D 955 |
| Mold Shrinkage, flow, 24 hrs | 1.81 | % | ISO 294 |
| Mold Shrinkage, xflow, 24 hrs | 1.83 | % | ISO 294 |
| Wear Factor Washer | 14 | 10^-10 in^5-min/ft-lb-hr | ASTM D 3702 Modified |
| Dynamic COF | 0.42 | - | ASTM D 3702 Modified |
| Static COF | 0.25 | - | ASTM D 3702 Modified |
| Density | 1.33 | g/cm³ | ISO 1183 |
| Moisture Absorption (23°C / 50% RH) | 4.28 | % | ISO 62 |
| ELECTRICAL | Value | Unit | Standard |
| Surface Resistivity | 1.E+09 - 1.E+11 | Ohm | ASTM D 257 |
| Source GMD, last updated:10/01/2004 | |||
| Parameter | ||
| Injection Molding | Value | Unit |
| Drying Temperature | 80 | °C |
| Drying Time | 4 | hrs |
| Melt Temperature | 195 - 205 | °C |
| Front - Zone 3 Temperature | 200 - 210 | °C |
| Middle - Zone 2 Temperature | 190 - 200 | °C |
| Rear - Zone 1 Temperature | 175 - 190 | °C |
| Mold Temperature | 70 - 95 | °C |
| Back Pressure | 0.2 - 0.3 | MPa |
| Screw Speed | 30 - 60 | rpm |
| Source GMD, last updated:10/01/2004 | ||
For more information please download the datasheet | |
 | Sabic Verton K3000Z.pdf |