WL-0082 Good Adhesion Water Based Acrylic Resin For Water-Based UV Curing Coating

Water Resistance Water Based Acrylic Resin Good Wettability Grinding To Pigments

WL-008-32 UV curable Water-based acrylic resins

Product Introduction

This product is mainly tetrafunctional waterborne acrylic synthetic resin. Acrylate-based UV-curable resins has a high solid content and is slightly harder overall, with fast curing speed and good surface drying effect. Good adhesion to the surface of plastic and paper. No pollution, low odor, low toxicity, non-combustibility; Waterborne UV curable resins can be used alone with water, initiators, additives, etc., or it can be blended with water-based or oily monomers or resins according to performance requirements, and combined with initiators, additives, etc. With the use of. Suitable for UV varnish, PET varnish, paint, ink, etc.

Physical Property:

Features

• Good adhesion to plastic and paper
• Good water resistance
• Good water solubility and dilution
• Good wettability and sandability to pigments
• High hardness
• Good compatibility with water

Application

• Water-based UV ink, varnish
• Water-based UV curing coating, industrial coatings (metal coatings)

Suggested formula:

Water-based paper uv varnish: WL-008-32: 70%; initiator 1173: 4-6%; triethanolamine: 2-3%; PM/isopropanol: 4-5%; ionized water: 10%; 10100:5 %; leveling agent: 0.3-0.5%; wetting agent: 0.3-0.5%; defoaming agent: 0.3-0.5%; wear-resistant wax: 0.5%.

Packaging and Storage Condition

• 20kg/ barrel, 200kg/ barrel. This product is not dangerous and can be transported as general cargo.
• The product should be stored in an airtight container to avoid freezing and high temperature. When possible, it should be used within six months. Recommended normal storage temperature is 10-35°

Special Tips

This material is complied according to our existing technology and experience, the technical advice provided is sincere, but it is not guaranteed to be used in all samples and formulations, all the data are for users reference only.