54mm Mixed Polypropylene Fiber Twister And Mesh Form For Concrete Reinforcing

City & Province	hefei

Product Details

54mm Mixed Polypropylene Fiber Twister And Mesh Form For Concrete Reinforcing

Products Description

Introduction

1. This fiber is used to instead of steel fiber for reinforcement
to cement concrete. Compared with steel fiber, it has the
advantage of easy dispersing and blending, no damage to the mixing
equipment, etc

2. The rigid polymer fiber is used polypropylene as its raw
material, produced the rough surface treatment by special parallel
thread extruding & twisting process. It has high break
strength, better dispersion and strong combining ability, will be
widely used to instead of steel fiber to reinforce the cement
concrete and crack-resistant.

Specification

Product namePP Fiber Bunchy Form
Diameter0.3+/-0.05 mm
Length48mm, 52mm, 54mm...
Tensile Strength> 600Mpa
Crack Elongation> 15%
Melting Point160-170
Elastic Modulus> 5000Mpa
Acid & Alkali ResistanceStrong
 

Apply Instruction:

1. Ration design of the fiber concrete:
Generally the recommended amount to add to the concrete is more
than 2.7kg per m3 (volume ratio is 0.3%), reinforcement adding
amount is 5.5kg, Compared with adding 47kg of steel fibre, 5.4kg
polymer fiber has the same volume ratio to the concrete.

2. Length: 54mm for common crack-resistant requirement.

3. Matching Ratio:
Usually, it is no need to Change the matching ratio of the
concrete. Considering the requirement of fissure-resistant, the
polymer fiber is recommend to combine with the PP fiber mesh form
with the volume ratio of 1:1 (0.9kg fiber-mesh to per m3 of cement
concrete).

4. Mixer Adoption: Double-axle horizontal compelling mixer is
priority.

5. Mixing process:
Crushed stones, fibers and sands are put into the mixer in
succession. After stirring for two minutes, fiber will fully spread
and then add cement and water and stir normally. The addition of
materials also can be put into as common concrete, but the stirring
time should be properly prolonged to make fiber completely mixed

6. Shaping & Maintenance:
There is no special requirement, may along the vibrating time for
30s, The maintenance of the fiber concrete should be done same as
the normal concrete.
 
Application
 
1. The surface of road, bridge, runway and floor of the factory.

2. Wall and roof of the tunnel and mine.

3. Dam, river, bridge pier, dock and military protection
facilities.
Product packaging
1)small PE bag of 1kg each each and then 10kgs each woven bag,
6MTS/1X20`FCL and 13MTS/1X40`HQ without pallet
2)small paper bag of 1kgs each and then 10kgs each box, about
3.6MTS/1X20`FCL or 9MTS/1X40`HQ with pallet.
 

Hot Products

White Powder B-VMCH Similar to VMCH of Dow Chemical For Primer And Inks For Golden And Silver Card Papers

White Powder B-VMCH Similar to VMCH of Dow Chemical For Primer And Inks For Golden And Silver Card ...

Degalan LP64/12 Thermoplastic Acrylic Resin BA-725 For Plastic Paint

Thermoplastic solid acrylic resin BA-725 (Be similar to Degalan LP 64/12 ) Resolvable: It is Solid ...

White Beads Solid Acrylic Resin BA-HV For Exterior Coating And Fire-Retardant Coating

White Beads Solid Acrylic Resin BA-HV For Exterior Coating And Fire-Retardant Coating Solid Acrylic ...

Softenting Point 185- 195℃ Solid Acrylic Resin BA-15 For Heat Transfer Printing

Softenting Point 185- 195℃ Solid Acrylic Resin BA-15 For Heat Transfer Printing Introduction: Solid ...

Solid Acrylic Resin BA-66 For Plastic Coating And Container Coating

Solid Acrylic Resin BA-66 For Plastic Coating And Container Coating Solid Acrylic resin Representati...

Excellent Adhesion Solid Acrylic Resin BA-44 For Fluorocarbon Coating And Paints And Inks

Excellent Adhesion Solid Acrylic Resin BA-44 For Fluorocarbon Coating And Paints and Inks Solid ...

Related Products

Product name	PP Fiber Bunchy Form
Diameter	0.3+/-0.05 mm
Length	48mm, 52mm, 54mm...
Tensile Strength	> 600Mpa
Crack Elongation	> 15%
Melting Point	160-170
Elastic Modulus	> 5000Mpa
Acid & Alkali Resistance	Strong